Resist composition and method of forming resist pattern

ABSTRACT

A resist composition including a compound (D0) represented by general formula (d0) and a resin component (A1) has a structural unit (a0) in which a compound represented by general formula (a0-1) has a polymerizable group within the W 1  portion converted into a main chain (in formula (d0), Rd 01  represents a fluorine atom or a fluorinated alkyl group; In formula (a0-1), W 1  represents a polymerizable group-containing group; C t  represents a tertiary carbon atom, and the α-position of C t  is a carbon atom which constitutes a carbon-carbon unsaturated bond; R 11  represents an aromatic hydrocarbon group; or a chain hydrocarbon group; R 12  and R 13  each independently represents a chain hydrocarbon group, or R 12  and R 13  are mutually bonded to form a cyclic group).

TECHNICAL FIELD

The present invention relates to a resist composition and a method of forming a resist pattern.

Priority is claimed on Japanese Patent Application No. 2018-226479, filed Dec. 3, 2018, the content of which is incorporated herein by reference.

DESCRIPTION OF RELATED ART

In lithography techniques, for example, a resist film composed of a resist material is formed on a substrate, and the resist film is subjected to selective exposure, followed by development, thereby forming a resist pattern having a predetermined shape on the resist film. A resist material in which the exposed portions of the resist film become soluble in a developing solution is called a positive-type, and a resist material in which the exposed portions of the resist film become insoluble in a developing solution is called a negative-type.

In recent years, in the production of semiconductor elements and liquid crystal display elements, advances in lithography techniques have led to rapid progress in the field of pattern miniaturization.

Typically, these miniaturization techniques involve shortening the wavelength (increasing the energy) of the exposure light source. Conventionally, ultraviolet radiation typified by g-line and i-line radiation has been used, but nowadays KrF excimer lasers and ArF excimer lasers are starting to be introduced in mass production. Furthermore, research is also being conducted into lithography techniques that use an exposure light source having a wavelength shorter (energy higher) than these excimer lasers, such as electron beam (EB), extreme ultraviolet radiation (EUV), and X ray.

In addition, currently, as the resist material in EUV lithography and EB lithography, chemically amplified resists proposed for KrF excimer laser and ArF excimer laser have been generally used since such chemically amplified resists exhibit excellent lithography properties, such as sensitivity to EUV and EB, and resolution sufficient to form a fine resist pattern as a target. In particular, chemically amplified resist containing an acrylic resin as the base material are known to be advantageous in such lithography properties.

Regarding the resist material, particularly in EUV exposure, acid diffusion control was a problem. For controlling acid diffusion, the anion structure of the acid generator is generally changed. Acid generators having an anion structure with a short acid diffusion length are already applied.

For further controlling acid diffusion, methods in which designs of polymeric compounds are variously changed have been employed.

For example, Patent Literature 1 describes a resist composition which employs a polymer compound having a specific acid-dissociable functional group (protecting group) to improve sensitivity to an exposure light source and improve resolution.

DOCUMENTS OF RELATED ART Patent Literature

[Patent Literature 1] WO2010/095698

SUMMARY OF THE INVENTION

As the lithography technique further progresses and the miniaturization of the resist pattern progresses more and more, for example, a target of the lithography performed by electron beams and EUV is to form fine resist patterns of several tens of nanometers. As the size of the resist pattern becomes smaller, the resist composition is required to have a high sensitivity to the exposure dose, and good lithography properties such as reduced roughness.

However, when a resist composition with high sensitivity as described in Patent Literature 1 is used in EUV lithography or EB lithography, the deprotection reaction of the protective group may proceed even in the unexposed portion of the resist film. Therefore, there were problems that the contrast between the exposed portions and the unexposed portions of the resist film is deteriorated, the film thickness of the unexposed portion is reduced, the roughness (surface roughness of the upper surface of the pattern and the side wall) occur, pattern disconnection (for example, in the case of a line and space pattern, defects in the width direction of the line) is likely to occur.

For example, in EUV lithography, light of a wavelength outside the EUV region, so-called OoB (Out of Band) light, which is included in light generated from a light source of an EUV exposure apparatus, is a problem. The OoB light enters the unexposed portion of the resist film as flare (stray light) (that is, the selectivity of the exposed area during EUV light irradiation is lost), and the acid generator component is decomposed and generates acid even in the unexposed portion. For this reason, the deprotection reaction of the protecting group proceeds in the unexposed portion, which causes a deterioration in contrast of the resist pattern, loss of film thickness, deterioration of roughness, pattern disconnection, and the like.

Also in EB lithography, depending on electron beam irradiation conditions such as acceleration voltage, electrons may diffuse (scatter) on the resist film surface and cause the same problem as the OoB light in the EUV lithography.

The deterioration in contrast and film thickness loss cause deterioration in resolution and the occurrence of roughness, pattern disconnection, and the like. Therefore, improvement in contrast and film thickness loss is demanded.

The present invention takes the above circumstances into consideration, with an object of providing a resist composition which exhibits improved sensitivity and lithography properties, and which is capable of forming a resist pattern having a good shape; and a method of forming a resist pattern using the resist composition.

For solving the above-mentioned problems, the present invention employs the following aspects.

Specifically, a first aspect of the present invention is a resist composition which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid, the resist composition including: a resin component (A1) which exhibits changed solubility in a developing solution under action of acid, and a compound (D0) represented by general formula (d0) shown below, the resin component (A1) has a structural unit (a0) in which a compound represented by general formula (a0-1) has a polymerizable group within the W¹ portion converted into a main chain.

In formula (d0), Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group; Rd⁰² represents a substituent; q represents an integer of 0 to 3; n1 represents an integer of 1 or more; n2 represents an integer of 0 or more; provided that n1+n2≤(q×2)+5; m represents an integer of 1 or more, and M^(m+) represents an m-valent organic cation. In formula (a0-1), W¹ represents a polymerizable group-containing group; C^(t) represents a tertiary carbon atom, and the α-position of C^(t) is a carbon atom which constitutes a carbon-carbon unsaturated bond; R¹¹ represents an aromatic hydrocarbon group which may have a substituent, or a chain hydrocarbon group; R¹² and R¹³ each independently represents a chain hydrocarbon group which may have a substituent, or R¹² and R¹³ are mutually bonded to form a cyclic group which may have a substituent.

A second aspect of the present invention is a method of forming a resist pattern, including: using a resist composition according to the first aspect to form a resist film, exposing the resist film, and developing the exposed resist film to form a resist pattern.

According to the present invention, there are provided a resist composition which exhibits improved sensitivity and lithography properties, and which is capable of forming a resist pattern having a good shape; and a method of forming a resist pattern using the resist composition.

DETAILED DESCRIPTION OF THE INVENTION

In the present description and claims, the term “aliphatic” is a relative concept used in relation to the term “aromatic”, and defines a group or compound that has no aromaticity.

The term “alkyl group” includes linear, branched or cyclic, monovalent saturated hydrocarbon, unless otherwise specified. The same applies for the alkyl group within an alkoxy group.

The term “alkylene group” includes linear, branched or cyclic, divalent saturated hydrocarbon, unless otherwise specified.

A “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of an alkyl group is substituted with a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.

A “fluorinated alkyl group” or a “fluorinated alkylene group” is a group in which part or all of the hydrogen atoms of an alkyl group or an alkylene group have been substituted with a fluorine atom.

The term “structural unit” refers to a monomer unit that contributes to the formation of a polymeric compound (resin, polymer, copolymer).

The case of describing “may have a substituent” includes both of the case where the hydrogen atom (—H) is substituted with a monovalent group and the case where the methylene group (—CH₂—) is substituted with a divalent group.

The term “exposure” is used as a general concept that includes irradiation with any form of radiation.

The term “base component” refers to an organic compound capable of forming a film, and is preferably an organic compound having a molecular weight of 500 or more. When the organic compound has a molecular weight of 500 or more, the film-forming ability is improved, and a resist pattern of nano level can be easily formed. The organic compound used as the base component is broadly classified into non-polymers and polymers. In general, as a non-polymer, any of those which have a molecular weight in the range of 500 to less than 4,000 is used. Hereafter, a “low molecular weight compound” refers to a non-polymer having a molecular weight in the range of 500 to less than 4,000. As a polymer, any of those which have a molecular weight of 1,000 or more is generally used. Hereafter, a “resin” or a “polymer” refers to a polymer having a molecular weight of 1,000 or more. As the molecular weight of the polymer, the weight average molecular weight in terms of the polystyrene equivalent value determined by gel permeation chromatography (GPC) is used.

A “structural unit derived from an acrylate ester” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of an acrylate ester.

An “acrylate ester” refers to a compound in which the terminal hydrogen atom of the carboxy group of acrylic acid (CH₂═CH—COOH) has been substituted with an organic group.

The acrylate ester may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent. The substituent (R^(α0)) that substitutes the hydrogen atom bonded to the carbon atom on the α-position is an atom other than hydrogen or a group, and examples thereof include an alkyl group of 1 to 5 carbon atoms and a halogenated alkyl group of 1 to 5 carbon atoms. Further, an acrylate ester having the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent (R^(α0)) in which the substituent has been substituted with a substituent containing an ester bond (e.g., an itaconic acid diester), or an acrylic acid having the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent (R^(α0)) in which the substituent has been substituted with a hydroxyalkyl group or a group in which the hydroxy group within a hydroxyalkyl group has been modified (e.g., α-hydroxyalkyl acrylate ester) can be mentioned as an acrylate ester having the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent. A carbon atom on the α-position of an acrylate ester refers to the carbon atom bonded to the carbonyl group, unless specified otherwise.

Hereafter, an acrylate ester having the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent is sometimes referred to as “α-substituted acrylate ester”. Further, acrylate esters and α-substituted acrylate esters are collectively referred to as “(α-substituted) acrylate ester”.

A “structural unit derived from acrylamide” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of acrylamide.

The acrylamide may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent, and may have either or both terminal hydrogen atoms on the amino group of acrylamide substituted with a substituent. A carbon atom on the α-position of an acrylamide refers to the carbon atom bonded to the carbonyl group, unless specified otherwise.

As the substituent which substitutes the hydrogen atom on the α-position of acrylamide, the same substituents as those described above for the substituent (R^(α0)) on the α-position of the aforementioned α-position of the aforementioned α-substituted acrylate ester can be mentioned.

A “structural unit derived from hydroxystyrene” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of hydroxystyrene. A “structural unit derived from a hydroxystyrene derivative” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of a hydroxystyrene derivative.

The term “hydroxystyrene derivative” includes compounds in which the hydrogen atom at the α-position of hydroxystyrene has been substituted with another substituent such as an alkyl group or a halogenated alkyl group; and derivatives thereof. Examples of the derivatives thereof include hydroxystyrene in which the hydrogen atom of the hydroxy group has been substituted with an organic group and may have the hydrogen atom on the α-position substituted with a substituent; and hydroxystyrene which has a substituent other than a hydroxy group bonded to the benzene ring and may have the hydrogen atom on the α-position substituted with a substituent. Here, the α-position (carbon atom on the α-position) refers to the carbon atom having the benzene ring bonded thereto, unless specified otherwise.

As the substituent which substitutes the hydrogen atom on the α-position of hydroxystyrene, the same substituents as those described above for the substituent on the α-position of the aforementioned α-substituted acrylate ester can be mentioned.

A “structural unit derived from vinylbenzoic acid or a vinylbenzoic acid derivative” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of vinylbenzoic acid or a vinylbenzoic acid derivative.

The term “vinylbenzoic acid derivative” includes compounds in which the hydrogen atom at the α-position of vinylbenzoic acid has been substituted with another substituent such as an alkyl group or a halogenated alkyl group; and derivatives thereof. Examples of the derivatives thereof include benzoic acid in which the hydrogen atom of the carboxy group has been substituted with an organic group and may have the hydrogen atom on the α-position substituted with a substituent; and benzoic acid which has a substituent other than a hydroxy group and a carboxy group bonded to the benzene ring and may have the hydrogen atom on the α-position substituted with a substituent. Here, the α-position (carbon atom on the α-position) refers to the carbon atom having the benzene ring bonded thereto, unless specified otherwise.

The term “styrene derivative” includes compounds in which the hydrogen atom at the α-position of styrene has been substituted with another substituent such as an alkyl group or a halogenated alkyl group; and derivatives thereof. Examples of the derivatives thereof include hydroxystyrene which has a substituent other than a hydroxy group bonded to the benzene ring and may have the hydrogen atom on the α-position substituted with a substituent. Here, the α-position (carbon atom on the α-position) refers to the carbon atom having the benzene ring bonded thereto, unless specified otherwise.

A “structural unit derived from styrene” or “structural unit derived from a styrene derivative” refers to a structural unit that is formed by the cleavage of the ethylenic double bond of styrene or a styrene derivative.

As the alkyl group as a substituent on the α-position, a linear or branched alkyl group is preferable, and specific examples include alkyl groups of 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group and a neopentyl group.

Specific examples of the halogenated alkyl group as the substituent on the α-position include groups in which part or all of the hydrogen atoms of the aforementioned “alkyl group as the substituent on the α-position” are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable.

Specific examples of the hydroxyalkyl group as the substituent on the α-position include groups in which part or all of the hydrogen atoms of the aforementioned “alkyl group as the substituent on the α-position” are substituted with a hydroxy group. The number of hydroxy groups within the hydroxyalkyl group is preferably 1 to 5, and most preferably 1.

In the present specification and claims, some structures represented by chemical formulae may have an asymmetric carbon, such that an enantiomer or a diastereomer may be present. In such a case, the one formula represents all isomers. The isomers may be used individually, or in the form of a mixture.

(Resist Composition)

The resist composition according to a first aspect of the present invention is a resist composition which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid, the resist composition including a base component (A) which exhibits changed solubility in a developing solution under action of acid (hereafter, also referred to as “component (A)”), and a compound (D0) represented by general formula (d0) (hereafter, also referred to as “component (D0)”). The component (A) includes a resin component (A1) (hereafter, also referred to as “component (A1)”) having a structural unit (a0) in which a compound represented by general formula (a0-1) has a polymerizable group within the W¹ portion converted into a main chain.

An example of one embodiment of the resist composition is a resist composition containing the component (A) and the component (D0) as a basic component (hereafter, also referred to as “component (D)”) which is capable of trapping acid generated upon exposure. Preferably, the resist composition contains, in addition to the component (A) and the component (D0), an acid-generator component (B) (hereafter, also referred to as “component (B)”) which generates acid upon exposure.

When a resist film is formed using the resist composition according to the present embodiment and the formed resist film is subjected to a selective exposure, acid is generated at exposed portions, and the generated acid acts on the component (A) to change the solubility of the component (A) in a developing solution, whereas the solubility of the component (A) in a developing solution is not changed at unexposed portions, thereby generating difference in solubility in a developing solution between exposed portions and unexposed portions. Therefore, by subjecting the resist film to development, the exposed portions of the resist film are dissolved and removed to form a positive-tone resist pattern in the case of a positive resist, whereas the unexposed portions of the resist film are dissolved and removed to form a negative-tone resist pattern in the case of a negative resist.

In the present specification, a resist composition which forms a positive resist pattern by dissolving and removing the exposed portions of the resist film is called a positive resist composition, and a resist composition which forms a negative resist pattern by dissolving and removing the unexposed portions of the resist film is called a negative resist composition.

The resist composition of the present embodiment may be either a positive resist composition or a negative resist composition. Further, in the present embodiment, the resist composition may be applied to an alkali developing process using an alkali developing solution in the developing treatment, or a solvent developing process using a developing solution containing an organic solvent (organic developing solution) in the developing treatment, and preferably a solvent developing process.

The resist composition of the present embodiment has a function of generating acid upon exposure, and the component (A) may generate acid upon exposure, in addition to the component (B).

In the case where the component (A) generates acid upon exposure, the component (A) is a “base component which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid”.

In the case where the component (A) is a base component which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid, the component (A1) described later is preferably a polymeric compound which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid. As the polymeric compound, a resin having a structural unit which generates acid upon exposure may be mentioned. As the structural unit which generates acid upon exposure, any conventionally known structural unit may be used.

<Component (A)>

In the resist composition of the present embodiment, the component (A) is a base component which exhibits changed solubility in a developing solution under action of acid.

In the present invention, the term “base component” refers to an organic compound capable of forming a film, and is preferably an organic compound having a molecular weight of 500 or more. When the organic compound has a molecular weight of 500 or more, the film-forming ability is improved, and a resist pattern of nano level can be easily formed.

The organic compound used as the base component is broadly classified into non-polymers and polymers.

In general, as a non-polymer, any of those which have a molecular weight in the range of 500 to less than 4,000 is used. Hereafter, a “low molecular weight compound” refers to a non-polymer having a molecular weight in the range of 500 to less than 4,000.

As a polymer, any of those which have a molecular weight of 1,000 or more is generally used. Hereafter, a “resin” or a “polymer” refers to a polymer having a molecular weight of 1,000 or more.

As the molecular weight of the polymer, the weight average molecular weight in terms of the polystyrene equivalent value determined by gel permeation chromatography (GPC) is used.

In the case where the resist composition of the present embodiment is a “negative resist composition for alkali developing process” which forms a negative resist pattern in an alkali developing process, or a “positive resist composition for solvent developing process”, as the component (A), a base component (A-2) which is soluble in an alkali developing solution (hereafter, referred to as “component (A-2)”) may be preferably used, and a cross-linking agent is blended. In such a resist composition, for example, when acid is generated from the component (B) upon exposure, the action of the acid causes cross-linking between the component (A-2) and the cross-linking component. As a result, the solubility of the resist composition in an alkali developing solution is decreased (the solubility of the resist composition in an organic developing solution is increased).

Therefore, in the formation of a resist pattern, by conducting selective exposure of a resist film formed by applying the resist composition to a substrate, the exposed portions of the resist film become insoluble in an alkali developing solution (soluble in an organic developing solution), whereas the unexposed portions of the resist film remain soluble in an alkali developing solution (insoluble in an organic developing solution), and hence, a negative resist pattern is formed by conducting development using an alkali developing solution. Alternatively, in such a case, by developing using an organic developing solution, a positive resist pattern is formed.

As the component (A-2), a resin that is soluble in an alkali developing solution (hereafter, referred to as “alkali-soluble resin”) is preferably used.

Examples of the alkali soluble resin include a resin having a structural unit derived from at least one of α-(hydroxyalkyl)acrylic acid and an alkyl ester of α-(hydroxyalkyl)acrylic acid (preferably an alkyl ester having 1 to 5 carbon atoms), as disclosed in Japanese Unexamined Patent Application, First Publication No. 2000-206694; an acrylic resin which has a sulfonamide group and may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent or polycycloolefin resin having a sulfoneamide group, as disclosed in U.S. Pat. No. 6,949,325; an acrylic resin which may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent and having a fluorinated alcohol, as disclosed in U.S. Pat. No. 6,949,325, Japanese Unexamined Patent Application, First Publication No. 2005-336452 or Japanese Unexamined Patent Application, First Publication No. 2006-317803; and a polycyclolefin resin having a fluorinated alcohol, as disclosed in Japanese Unexamined Patent Application, First Publication No. 2006-259582. These resins are preferable in that a resist pattern can be formed with minimal swelling.

Here, the term “α-(hydroxyalkyl)acrylic acid” refers to one or both of acrylic acid in which a hydrogen atom is bonded to the carbon atom on the α-position having the carboxyl group bonded thereto, and α-hydroxyalkylacrylic acid in which a hydroxyalkyl group (preferably a hydroxyalkyl group of 1 to 5 carbon atoms) is bonded to the carbon atom on the α-position.

As the cross-linking agent, typically, an amino-based cross-linking agent such as a glycoluril having a methylol group or alkoxymethyl group, or a melamine-based cross-linking agent is preferable, as it enables formation of a resist pattern with minimal swelling. The amount of the cross-linker added is preferably within a range from 1 to 50 parts by weight, relative to 100 parts by weight of the alkali-soluble resin.

In the case where the resist composition of the present embodiment is a “positive resist composition for alkali developing process” which forms a positive resist pattern in an alkali developing process, or a “negative resist composition for solvent developing process”, as the component (A), a base component (A-1) which exhibits increased polarity by the action of acid (hereafter, referred to as “component (A-1)”) may be preferably used. By using the component (A-1), since the polarity of the base component changes prior to and after exposure, an excellent development contrast can be obtained not only in an alkali developing process, but also in a solvent developing process.

More specifically, in the case of applying an alkali developing process, the component (A-1) is substantially insoluble in an alkali developing solution prior to exposure, but when acid is generated from the component (B) upon exposure, the action of this acid causes an increase in the polarity of the base component, thereby increasing the solubility of the component (A-1) in an alkali developing solution. Therefore, in the formation of a resist pattern, by conducting selective exposure of a resist film formed by applying the resist composition to a substrate, the exposed portions of the resist film change from an insoluble state to a soluble state in an alkali developing solution, whereas the unexposed portions of the resist film remain insoluble in an alkali developing solution, and hence, a positive resist pattern is formed by alkali developing.

On the other hand, in the case of a solvent developing process, the component (A-1) exhibits high solubility in an organic developing solution prior to exposure, and when acid is generated from the component (B) upon exposure, the polarity of the component (A-1) is increased by the action of the generated acid, thereby decreasing the solubility of the component (A-1) in an organic developing solution. Therefore, in the formation of a resist pattern, by conducting selective exposure of a resist film formed by applying the resist composition to a substrate, the exposed portions of the resist film changes from an soluble state to an insoluble state in an organic developing solution, whereas the unexposed portions of the resist film remain soluble in an organic developing solution. As a result, by conducting development using an organic developing solution, a contrast can be made between the exposed portions and unexposed portions, thereby forming a negative resist pattern.

In the resist composition of the present embodiment, as the component (A), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

In the resist composition of the present embodiment, the component (A) is preferably a component (A-1). That is, the resist composition of the present embodiment is preferably a resist composition which forms a positive pattern in an alkali developing process (i.e, a positive resist compound for alkali developing process) or a resist composition which forms a negative pattern in a solvent developing process (i.e., a negative type resist composition for solvent developing process). As the component (A), at least one of a polymeric compound and a low molecular weight compound may be used.

In the case where the component (A) is a component (A-1), the component (A-1) preferably contains a resin component (A1) (hereafter, referred to as “component (A1)”).

Component (A1)

The component (A1) is a resin component having a structural unit (a0) in which a compound represented by general formula (a0-1) has a polymerizable group within the W¹ portion converted into a main chain.

If desired, the component (A1) may include, in addition to the structural unit (a0), other structural unit.

<<Structural Unit (a0)>>

The structural unit (a0) is a structural unit in which a compound represented by general formula (a0-1) has a polymerizable group within the W¹ portion converted into a main chain.

The “polymerizable group” in the W¹ portion is a group that allows a compound having a polymerizable group to be polymerized by radical polymerization or the like, for example, a group containing a carbon-carbon multiple bond such as an ethylenic double bond.

“A polymerizable group has been converted to a main chain” means that the multiple bond within the polymerizable group has been cleaved to form a main chain. For example, in the case of a monomer having an ethylenic double bond, the ethylenic double bond is cleaved such that the carbon-carbon single bond forms a main chain.

In formula (a0-1), W¹ represents a polymerizable group-containing group; C^(t) represents a tertiary carbon atom, and the α-position of C^(t) is a carbon atom which constitutes a carbon-carbon unsaturated bond; R¹¹ represents an aromatic hydrocarbon group which may have a substituent, or a chain hydrocarbon group; R¹² and R¹³ each independently represents a chain hydrocarbon group which may have a substituent, or R¹² and R¹³ are mutually bonded to form a cyclic group which may have a substituent.

In general formula (a0-1), W¹ represents a polymerizable group-containing group.

Examples of the polymerizable group for the W¹ portion include a vinyl group, an allyl group, an acryloyl group, a methacryloyl group, a fluorovinyl group, a difluorovinyl group, a trifluorovinyl group, a difluorotrifluoromethylvinyl group, a trifluoroallyl group, a perfluoroallyl group, a trifluoromethylacryloyl group, a nonylfluorobutylacryloyl group, a vinyl ether group, a fluorine-containing vinyl ether group, an allyl ether group, an fluorine-containing allyl ether group, a styryl group, a vinylnaphthyl group, a fluorine-containing styryl group, a fluorine-containing vinylnaphthyl group, a norbornyl group, a fluorine-containing norbornyl group, and a silyl group.

The polymerizable group-containing group may be a group constituted of only a polymerizable group, or a group constituted of a polymerizable group and a group other than a polymerizable group. Examples of the group other than a polymerizable group include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom.

Preferable examples of W¹ include a group represented by the chemical formula: C(R^(X11))(R^(X12))═C(R^(X13))—Ya^(x0)—.

In the chemical formula, R^(X11), R^(X12) and R^(X13) independently represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, and Ya^(x0) represents a single bond or a divalent linking group.

In the chemical formula, as the alkyl group of 1 to 5 carbon atoms for R^(X11), R^(X12) and R^(X13), a linear or branched alkyl group of 1 to 5 carbon atoms is preferable, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group and a neopentyl group. The halogenated alkyl group of 1 to 5 carbon atoms represented by R is a group in which part or all of the hydrogen atoms of the aforementioned alkyl group of 1 to 5 carbon atoms have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable.

Among these examples, as R^(X11) and R^(X12) a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and in terms of industrial availability, a hydrogen atom or a methyl group is more preferable, and a hydrogen atom is still more preferable.

As R^(X13), a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and in terms of industrial availability, a hydrogen atom or a methyl group is more preferable.

In the aforementioned chemical formula, the divalent linking group for Ya^(x0) is not particularly limited, and preferable examples thereof include a divalent hydrocarbon group which may have a substituent and a divalent linking group containing a hetero atom.

Divalent Hydrocarbon Group which May have a Substituent:

In the case where Ya^(x0) is a divalent linking group which may have a substiuent, the hydrocarbon group may be either an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

Aliphatic Hydrocarbon Group for Ya^(x0)

The “aliphatic hydrocarbon group” refers to a hydrocarbon group that has no aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated. In general, the aliphatic hydrocarbon group is preferably saturated.

Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in the structure thereof can be given.

Linear or Branched Aliphatic Hydrocarbon Group

The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, still more preferably 1 to 4, and most preferably 1 to 3.

As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specific examples thereof include a methylene group [—CH₂—], an ethylene group [—(CH₂)₂—], a trimethylene group [—(CH₂)₃—], a tetramethylene group [—(CH₂)₄-] and a pentamethylene group [—(CH₂)₅—].

The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6, still more preferably 3 or 4, and most preferably 3.

As the branched aliphatic hydrocarbon group, branched alkylene groups are preferred, and specific examples include various alkylalkylene groups, including alkylmethylene groups such as —CH(CH₃)—, —CH(CH₂CH₃)—, —C(CH₃)₂—, —C(CH₃)(CH₂CH₃)—, —C(CH₃)(CH₂CH₂CH₃)—, and —C(CH₂CH₃)₂—; alkylethylene groups such as —CH(CH₃)CH₂—, —CH(CH₃)CH(CH₃)—, —C(CH₃)₂CH₂—, —CH(CH₂CH₃)CH₂—, and —C(CH₂CH₃)₂—CH₂—; alkyltrimethylene groups such as —CH(CH₃)CH₂CH₂—, and —CH₂CH(CH₃)CH₂—; and alkyltetramethylene groups such as —CH(CH₃)CH₂CH₂CH₂—, and —CH₂CH(CH₃)CH₂CH₂—. As the alkyl group within the alkylalkylene group, a linear alkyl group of 1 to 5 carbon atoms is preferable.

The linear or branched aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group of 1 to 5 carbon atoms, and a carbonyl group.

Aliphatic Hydrocarbon Group Containing a Ring in the Structure Thereof

As examples of the hydrocarbon group containing a ring in the structure thereof, a cyclic aliphatic hydrocarbon group containing a hetero atom in the ring structure thereof and may have a substituent (a group in which two hydrogen atoms have been removed from an aliphatic hydrocarbon ring), a group in which the cyclic aliphatic hydrocarbon group is bonded to the terminal of the aforementioned chain-like aliphatic hydrocarbon group, and a group in which the cyclic aliphatic group is interposed within the aforementioned linear or branched aliphatic hydrocarbon group, can be given. As the linear or branched aliphatic hydrocarbon group, the same groups as those described above can be used.

The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.

The cyclic aliphatic hydrocarbon group may be either a polycyclic group or a monocyclic group. As the monocyclic aliphatic hydrocarbon group, a group in which 2 hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. As the polycyclic group, a group in which 2 hydrogen atoms have been removed from a polycycloalkane is preferable, and the polycyclic group preferably has 7 to 12 carbon atoms. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane and tetracyclododecane.

The cyclic aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group and a carbonyl group.

The alkyl group as the substituent is preferably an alkyl group of 1 to 5 carbon atoms, and a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group is particularly desirable.

The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group or tert-butoxy group, and most preferably a methoxy group or an ethoxy group.

Examples of the halogen atom for the substituent include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.

Examples of the halogenated alkyl group for the substituent include groups in which part or all of the hydrogen atoms within the aforementioned alkyl groups has been substituted with the aforementioned halogen atoms.

The cyclic aliphatic hydrocarbon group may have part of the carbon atoms constituting the ring structure thereof substituted with a substituent containing a hetero atom. As the substituent containing a hetero atom, —O—, —C(═O)—O—, —S—, —S(═O)₂— or —S(═O)₂—O— is preferable.

Aromatic Hydrocarbon Group for Ya^(x0)

The aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring.

The aromatic ring is not particularly limited, as long as it is a cyclic conjugated compound having (4n+2)π electrons, and may be either monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, and still more preferably 6 to 15 carbon atoms, and most preferably 6 to 12 carbon atoms. Here, the number of carbon atoms within a substituent(s) is not included in the number of carbon atoms of the aromatic hydrocarbon group. Examples of the aromatic ring include aromatic hydrocarbon rings, such as benzene, naphthalene, anthracene and phenanthrene; and aromatic hetero rings in which part of the carbon atoms constituting the aforementioned aromatic hydrocarbon rings has been substituted with a hetero atom. Examples of the hetero atom within the aromatic hetero rings include an oxygen atom, a sulfur atom and a nitrogen atom. Specific examples of the aromatic hetero ring include a pyridine ring and a thiophene ring.

Specific examples of the aromatic hydrocarbon group include a group in which two hydrogen atoms have been removed from the aforementioned aromatic hydrocarbon ring or aromatic hetero ring (arylene group or heteroarylene group); a group in which two hydrogen atoms have been removed from an aromatic compound having two or more aromatic rings (biphenyl, fluorene or the like); and a group in which one hydrogen atom of the aforementioned aromatic hydrocarbon ring or aromatic hetero ring has been substituted with an alkylene group (a group in which one hydrogen atom has been removed from the aryl group within the aforementioned arylalkyl group such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, or a 2-naphthylethyl group, or a heteroarylalkyl group). The alkylene group which is bonded to the aforementioned aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 or 2 carbon atoms, and most preferably 1 carbon atom.

With respect to the aromatic hydrocarbon group, the hydrogen atom within the aromatic hydrocarbon group may be substituted with a substituent. For example, the hydrogen atom bonded to the aromatic ring within the aromatic hydrocarbon group may be substituted with a substituent. Examples of substituents include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxyl group.

The alkyl group as the substituent is preferably an alkyl group of 1 to 5 carbon atoms, and a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group is particularly desirable.

As the alkoxy group, the halogen atom and the halogenated alkyl group for the substituent, the same groups as the aforementioned substituent groups for substituting a hydrogen atom within the cyclic aliphatic hydrocarbon group can be used.

Divalent Linking Group Containing a Hetero Atom

In the case where Ya^(x0) represents a divalent linking group containing a hetero atom, preferable examples of the linking group include —O—, —C(═O)—O—, —C(═O)—, —O—C(═O)—O—, —C(═O)—NH—, —NH—, —NH—C(═NH)— (may be substituted with a substituent such as an alkyl group, an acyl group or the like), —S—, —S(═O)₂—, —S(═O)₂—O—, and a group represented by general formula: —Y²¹—O—Y²²—, —Y²¹—O—, —Y²¹—C(═O)—O—, —C(═O)—O—Y²¹—, —[Y²¹—C(═O)—O]_(m″)—Y²²—, —Y²¹—O—C(═O)—Y²²— or —Y²¹—S(═O)₂—O—Y²²— [in the formulae, Y²¹ and Y²² each independently represents a divalent hydrocarbon group which may have a substituent, O represents an oxygen atom, and m′ represents an integer of 0 to 3].

In the case where the divalent linking group containing a hetero atom is —C(═O)—NH—, —C(═O)—NH—C(═O)—, —NH— or —NH—C(═NH)—, H may be substituted with a substituent such as an alkyl group, an acyl group or the like. The substituent (an alkyl group, an acyl group or the like) preferably has 1 to 10 carbon atoms, more preferably 1 to 8, and most preferably 1 to 5.

In general formulae —Y²¹—O—Y²²—, —Y²¹—O—, —Y²¹—C(═O)—O—, —C(═O)—O—Y²¹—, —[Y²¹—C(═O)—O]_(m″)—Y²²—, —Y²¹—O—C(═O)—Y²²— or —Y²¹—S(═O)₂—O—Y²²—, Y²¹ and Y²² each independently represents a divalent hydrocarbon group which may have a substituent. Examples of the divalent hydrocarbon group include the same groups as those described above as the “divalent hydrocarbon group which may have a substituent” in the explanation of the aforementioned divalent linking group.

As Y²¹, a linear aliphatic hydrocarbon group is preferable, more preferably a linear alkylene group, still more preferably a linear alkylene group of 1 to 5 carbon atoms, and a methylene group or an ethylene group is particularly desirable.

As Y²², a linear or branched aliphatic hydrocarbon group is preferable, and a methylene group, an ethylene group or an alkylmethylene group is more preferable. The alkyl group within the alkylmethylene group is preferably a linear alkyl group of 1 to 5 carbon atoms, more preferably a linear alkyl group of 1 to 3 carbon atoms, and most preferably a methyl group.

In the group represented by the formula —[Y²¹—C(═O)—O]_(m″)—Y²²—, m″ represents an integer of 0 to 3, preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 1. Namely, it is particularly desirable that the group represented by the formula —[Y²¹—C(═O)—O]_(m″)—Y²²— is a group represented by the formula —Y²¹—C(═O)—O—Y²²—. Among these, a group represented by the formula —(CH₂)_(a′)—C(═O)—O—(CH₂)_(b′)— is preferable. In the formula, a′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, still more preferably 1 or 2, and most preferably 1. b′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, still more preferably 1 or 2, and most preferably 1.

Among these examples, as Ya^(x0), an ester bond [—C(═O)—O—, —O—C(═O)—], an ether bond (—O—), a linear or branched alkylene group, an aromatic hydrocarbon group, or a combination thereof, or a single bond is preferable. Among these, as Ya^(x0), an ester bond [—C(═O)—O—, —O—C(═O)—], a linear or branched alkylene group, or a combination thereof, or a single bond is more preferable, and a single bond is most preferable.

In formula (a0-1), C^(T) represents a tertiary carbon atom, and the α-position of C^(t) is a carbon atom which constitutes a carbon-carbon unsaturated bond.

The “α-position of C^(t)” refers to the first carbon atom adjacent to the carbon atom (C^(t)) bonded to the oxy group (—O—) in formula (a0-1).

In formula (a0-1), “—C^(t)(R¹¹)(R¹²)(R¹³)” is an acid dissociable group. The acid dissociable group protects the oxy group (—O—) side of the carbonyloxy group [—C(═O)—O—] in formula (a0-1). An “acid dissociable group” exhibits acid dissociability such that the bond between the acid dissociable group and the adjacent oxygen atom (O) is cleaved by the action of acid. When the acid dissociable group is dissociated by the action of acid, a polar group which exhibits a higher polarity than the acid dissociable group is generated, and the polarity is increased. As a result, the polarity of the entire component (A1) is increased. By the increase in the polarity, the solubility in an alkali developing solution changes, and the solubility in an alkali developing solution is relatively increased, whereas the solubility in an organic developing solution is relatively decreased.

In formula (a0-1), at least one of R¹¹, R¹² and R¹³ has a carbon atom constituting a carbon-carbon unsaturated bond at the α-position of C^(t).

In formula (a0-1), R¹¹ represents an aromatic hydrocarbon group which may have a substituent, or a chain hydrocarbon group.

Examples of the aromatic hydrocarbon group for R¹¹ include a group in which 1 or more hydrogen atoms have been removed from an aromatic hydrocarbon ring having 5 to 30 carbon atoms. Among these examples, as R¹¹, a group in which 1 hydrogen atom has been removed from an aromatic hydrocarbon group of 6 to 15 carbon atoms is preferable, a group in which 1 hydrogen atom has been removed from benzene, naphthalene, anthracene or phenanthrene is more preferable, a group in which 1 hydrogen atom has been removed from benzene, naphthalene or anthracene is still more preferable, and a group in which 1 hydrogen atom has been removed from benzene is most preferable.

Examples of the substituent for R¹¹ include a methyl group, an ethyl group, a propyl group, a hydroxyl group, a carboxyl group, a halogen atom (a fluorine atom, a chlorine atom, a bromine atom, or the like), an alkoxy group (a methoxy group, an ethoxy group, a propoxy group, a butoxy group, or the like), and an alkyloxycarbonyl group.

The chain hydrocarbon group for R¹¹ may be a saturated hydrocarbon group or an unsaturated hydrocarbon group, and may be linear or branched.

The linear saturated hydrocarbon group (alkyl group) for R¹¹ preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, still more preferably 1 to 4 carbon atoms, and most preferably 1 or 2 carbon atoms. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group and an n-pentyl group. Among these, a methyl group, an ethyl group or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.

The branched alkyl group for R¹¹ preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include an isopropyl group, an isobutyl group, a tert-butyl group, an isopentyl group, a neopentyl group a 1,1-diethylpropyl group and a 2,2-dimethylbutyl group. Among these, an isopropyl group is preferable.

Examples of the unsaturated hydrocarbon group for R¹¹ include an alkenyl group.

The alkenyl group for R¹¹ preferably has 2 to 10 carbon atoms, more preferably 2 to 5 carbon atoms, still more preferably 2 to 4 carbon atoms, and most preferably 3 carbon atoms. Examples of linear alkenyl groups include a vinyl group, a propenyl group (an allyl group) and a butynyl group. Examples of branched alkenyl groups include a 1-methylvinyl group, a 2-methylvinyl group, a 1-methylpropenyl group and a 2-methylpropenyl group. Among these examples, as the chain-like alkenyl group, a linear alkenyl group is preferable, a vinyl group or a propenyl group is more preferable, and a vinyl group is most preferable.

In formula (a0-1), R¹² and R¹³ each independently represents a chain hydrocarbon group which may have a substituent, or R¹² and R¹³ are mutually bonded to form a cyclic group which may have a substituent.

The chain hydrocarbon group for R¹² and R¹³ is the same as defined for the chain hydrocarbon group for R¹¹. Further, the substituent for the chain hydrocarbon group represented by R¹² or R¹³ is the same as defined for the substituent for the chain hydrocarbon group represented by R¹¹.

In the case where R¹² and R¹³ are mutually bonded to form a cyclic group, the cyclic group may be a polycyclic group or a monocyclic group. Further, the cyclic group may be an alicyclic hydrocarbon group or a condensed polycyclic hydrocarbon group in which an alicyclic hydrocarbon group is fused with an aromatic ring.

As the monocyclic aliphatic hydrocarbon group, a group in which 1 hydrogen atom has been removed from a monocycloalkane or a monocycloalkene is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The monocycloalkene preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentene and cyclohexene.

As the polycyclic aliphatic hydrocarbon group, a group in which 1 hydrogen atom has been removed from a polycycloalkane or a polycycloalkene is preferable. The polycycloalkane preferably has 7 to 12 carbon atoms, and examples thereof include adamantane, norbornane, isobornane, tricyclodecane and tetracyclododecane. The polycycloalkene preferably has 7 to 12 carbon atoms, and examples thereof include adamantene, norbornene, isobornene, tricyclodecene and tetracyclododecene.

Examples of the condensed polycyclic hydrocarbon group in which an aromatic ring is fused with an alicyclic hydrocarbon group include a group in which one hydrogen atom has been removed from an aliphatic ring of a bicyclic compound, such as tetrahydronaphthalene or indane.

The cyclic group which is formed by the R¹² group and the R¹³ group being mutually bonded may have a substituent. Examples of the substituent for the cyclic hydrocarbon group formed by Xa⁰ together with Ya⁰ include —R^(P1), —R^(P2)—O—R^(P1), —R^(P2)—CO—R^(P1), —R^(P2)—CO—OR^(P1), —R^(P2)—O—CO—R^(P1), —R^(P2)—OH, —R^(P2)—CN and —R^(P2)—COOH ((hereafter, these substituents are sometimes collectively referred to as “Ra⁰⁶”).

Here, R^(P1) is a monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms, a monovalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms. Further, R^(P2) is a single bond, a divalent chain saturated hydrocarbon group having 1 to 10 carbon atoms, a divalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a divalent aromatic hydrocarbon group having 6 to 30 carbon atoms.

Here, a portion or all of the hydrogen atoms having the chain saturated hydrocarbon group, the aliphatic cyclic saturated hydrocarbon group, and the aromatic hydrocarbon group for R^(P1) and R^(P2) may be substituted with a fluorine atom. The aliphatic cyclic hydrocarbon group may have 1 or more substituents of 1 kind, or 1 or more substituents of a plurality of kinds.

Examples of the monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a decyl group.

Examples of the monovalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms include a monocyclic aliphatic saturated hydrocarbon group such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclodecyl group, and a cyclododecyl group; and a polycyclic aliphatic saturated hydrocarbon group such as a bicyclo[2.2.2]octanyl group, a tricyclo[5.2.1.02,6]decanyl group, a tricyclo[3.3.1.13,7]decanyl group, a tetracyclo[6.2.1.13,6.02,7]dodecanyl group, and an adamantyl group.

Examples of the monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms include a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene.

Among these examples, as the cyclic group formed by the R¹² group and the R¹³ group being mutually bonded, an alicyclic hydrocarbon group which may have a substituent is preferable, a monocyclic aliphatic hydrocarbon group which may have a substituent is more preferable, a group in which 1 hydrogen atom has been removed from a monocycloalkane or a monocycloalkene is still more preferable, and in terms of reactivity, a group in which 1 hydrogen atom has been removed from cyclopentane or cyclohexane is most preferable.

In formula (a0-1), preferable examples of the acid dissociable group represented by “—C^(t)(R¹¹)(R¹²)(R¹³)” include a group represented by general formula (a0-r-1) shown below, a group represented by general formula (a0-r-2) shown below, and a group represented by general formula (a0-r-3) shown below.

In formula (a0-r-1), Ra′¹¹⁰ represents a linear or branched alkyl group having 1 to 12 carbon atoms optionally having part thereof substituted with a halogen atom or a hetero atom-containing group; Ra′¹¹¹ represents a group which forms an aliphatic cyclic group together with the carbon atom to which Ra′¹¹⁰ is bonded, or a group which forms a condensed polycyclic hydrocarbon group containing an aliphatic ring, together with the carbon atom to which Ra′¹¹⁰ is bonded; wherein part or all of the hydrogen atoms of the aliphatic cyclic group or the condensed polycyclic hydrocarbon group may be substituted; provided that, in the aliphatic cyclic group or the condensed polycyclic hydrocarbon group, the α-position of the carbon atom bonded to Ra′¹¹⁰ is a carbon atom constituting a carbon-carbon unsaturated bond.

In formula (a0-r-2), C^(t) represents a tertiary carbon atoms; Xa represents an aliphatic cyclic group together with C^(t); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰¹ to Ra⁰³ each independently represents a hydrogen atom, a monovalent saturated chain hydrocarbon group of 1 to 10 carbon atoms or a monovalent saturated aliphatic cyclic hydrocarbon group of 3 to 20 carbon atoms; wherein part or all of the hydrogen atoms of the saturated chain hydrocarbon or the saturated aliphatic cyclic hydrocarbon may be substituted; 2 or more of Ra⁰¹ to Ra⁰³ may be mutually bonded to form an aliphatic cyclic structure, but does not form a bridged structure.

In formula (a0-r-3), C^(t) represents a tertiary carbon atoms; Xaa represents an aliphatic cyclic group together with ^(CT); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰⁴ represents an aromatic hydrocarbon group which may have a substituent; * represents a bonding site.

In formula (a0-r-1), Ra′¹¹⁰ represents a linear or branched alkyl group having 1 to 12 carbon atoms optionally having part thereof substituted with a halogen atom or a hetero atom-containing group.

The linear alkyl group for Ra′¹¹⁰ has 1 to 12 carbon atoms, preferably 1 to 10 carbon atoms, and more preferably 1 to 5 carbon atoms. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group and an n-pentyl group. Among these, a methyl group, an ethyl group or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.

The branched alkyl group for Ra′¹¹⁰ preferably has 3 to 10 carbon atoms, and more preferably 3 to 6 carbon atoms. Specific examples include an isopropyl group, an isobutyl group, a tert-butyl group, an isopentyl group, a neopentyl group, a 1,1-diethylpropyl group, a 1,1-dimethylbutyl group, a 1,1-dimethylpentyl group and a 2,2-dimethylbutyl group. Among these examples, an isopropyl group or a tert-butyl group is preferable.

The alkyl group for Ra′¹¹⁰ may have part thereof substituted with a halogen atom or a hetero atom-containing group. For example, part of the hydrogen atoms constituting the alkyl group may be substituted with a halogen atom or a hetero atom-containing group. Further, for example, part of the carbon atoms constituting the alkyl group (e.g., a methylene group) may be substituted with a hetero atom-containing group.

Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom. Examples of the hetero atom include an oxygen atom, a sulfur atom and a nitrogen atom. Examples of the hetero atom-containing group include an oxygen atom (—O—), —C(═O)—O—, —O—C(═O)—, —C(═O)—, —O—C(═O)—O—, —C(═O)—NH—, —NH—, —S—, —S(═O)₂— and —S(═O)₂—O—.

In formula (a0-r-1), Ra′¹¹¹ (the aliphatic cyclic group or condensed polycyclic hydrocarbon group together with the carbon atom bonded to Ra′¹¹⁰) is the same as defined for the monocyclic or polycyclic aliphatic hydrocarbon group or condensed polycyclic hydrocarbon group formed by R¹² and R¹³ being mutually bonded in the aforementioned formula (a0-1), and a monocyclic or polycyclic aliphatic hydrocarbon group (a group in which 1 hydrogen atom has been removed from a monocycloalkane or a group in which 1 hydrogen atom has been removed from a polycycloalkane) is preferable. The aliphatic cyclic group may be an unsaturated aliphatic cyclic group, and examples thereof include a group in which 1 hydrogen atom has been removed from a monocycloalkene, and a group in which 1 hydrogen atom has been removed from a polycycloalkene.

The aliphatic cyclic group for Ra′¹¹¹ may have a substituent. Examples of the substituent include the aforementioned substituent “Ra⁰⁶”, a divalent group which substitutes 2 hydrogen atoms of a methylene group (—CH₂—) (such as a methylidene group (═CH₂) or an ethylidene group). As the aliphatic cyclic group having a substituent, a group in which the divalent group is bonded at an α-position of the tertiary carbon atom in formula (a0-r-1) is preferable.

In formula (a0-r-2), C^(t) represents a tertiary carbon atoms.

In formula (a0-r-2), Xa represents a group which forms an aliphatic cyclic group together with C^(t). wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted;

As the aliphatic cyclic group formed by Xa and C^(t), the same groups as those described above for the monocyclic or polycyclic aliphatic hydrocarbon group (a group in which 1 hydrogen atom has been removed from a monocycloalkane or a group in which 1 hydrogen atom has been removed from a polycycloalkane) formed by R¹² and R¹³ being mutually bonded in the aforementioned formula (a0-1) is preferable.

As the substituent for the aliphatic cyclic group formed by Xa and C^(t), for example, the same groups as those defined for the aforementioned Ra⁰⁶ may be mentioned.

In formula (a0-r-2), Ra⁰¹ to Ra⁰³ each independently represents a hydrogen atom, a monovalent saturated chain hydrocarbon group of 1 to 10 carbon atoms or a monovalent saturated aliphatic cyclic hydrocarbon group of 3 to 20 carbon atoms, provided that part or all of the hydrogen atoms of the saturated chain hydrocarbon or the saturated aliphatic cyclic hydrocarbon may be substituted; 2 or more of Ra⁰¹ to Ra⁰³ may be mutually bonded to form an aliphatic cyclic structure, but does not form a bridged structure.

In formula (a0-r-2), examples of the monovalent saturated chain hydrocarbon group of 1 to 10 carbon atoms for Ra⁰¹ to Ra⁰³ include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a decyl group.

Examples of the monovalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms for Ra⁰¹ to Ra⁰³ include a monocyclic aliphatic saturated hydrocarbon group such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclodecyl group, and a cyclododecyl group; and a polycyclic aliphatic saturated hydrocarbon group such as a bicyclo[2.2.2]octanyl group, a tricyclo[5.2.1.02,6]decanyl group, a tricyclo[3.3.1.13,7]decanyl group, a tetracyclo[6.2.1.13,6.02,7]dodecanyl group, and an adamantyl group.

Among these examples, in terms of ease in synthesis of the compound (a0-1), Ra⁰¹ to Ra⁰³ is preferably a hydrogen atom or a monovalent saturated hydrocarbon group having 1 to 10 carbon atoms, more preferably a hydrogen atom, a methyl group or an ethyl group, and most preferably a hydrogen atom.

As the substituent for the saturated chain hydrocarbon group or saturated cyclic aliphatic hydrocarbon group represented by Ra⁰¹ to Ra⁰³, for example, the same substituents as those described above for Ra⁰⁶ may be mentioned.

Examples of the group containing a carbon-carbon double bond which is generated by forming a cyclic structure in which two or more of Ra⁰¹ to Ra⁰³ are bonded to each other include a cyclopentenyl group, a cyclohexenyl group, a methyl cyclopentenyl group, a methyl cyclohexenyl group, a cyclopentylideneethenyl group, and a cyclohexylidenethenyl group. Among these examples, in terms of ease in synthesis of the compound (a0-1), a cyclopentenyl group, a cyclohexenyl group or a cyclopentylideneethenyl group is preferable.

In formula (a0-r-3), C^(t) represents a tertiary carbon atoms.

In formula (a0-r-3), Xaa represents a group which forms a 5-membered aliphatic monocyclic group together with C^(t). provided that part or all of the hydrogen atoms of the 5-membered monocyclic aliphatic hydrocarbon group may be substituted;

As the aliphatic cyclic group formed by Xaa and C^(t), the same groups as those described above for the monocyclic or polycyclic aliphatic hydrocarbon group (a group in which 1 hydrogen atom has been removed from a monocycloalkane or a group in which 1 hydrogen atom has been removed from a polycycloalkane) formed by R¹² and R¹³ being mutually bonded in the aforementioned formula (a0-1) is preferable.

As the substituent for the aliphatic cyclic group formed by Xaa and C^(t), for example, the same groups as those defined for the aforementioned Ra⁰⁶ may be mentioned.

In formula (a0-r-3), Ra⁰⁴ represents an aromatic hydrocarbon group which may have a substituent. Examples of the aromatic hydrocarbon group for Ra⁰⁴ include the same aromatic hydrocarbon groups as those for R¹¹. Among these examples, as Ra⁰⁴, a group in which 1 or more hydrogen atoms have been removed from an aromatic hydrocarbon ring having 6 to 15 carbon atoms is preferable, and a group in which 1 or more hydrogen atoms have been removed from benzene is more preferable.

As the substituent for Ra⁰⁴, the same substituents as those described above for the aromatic hydrocarbon group represented by R¹¹ may be mentioned.

Specific examples of the group represented by the aforementioned formula (a0-r-1) are shown below. * indicates the bonding site with the oxy group (—O—).

Specific examples of the group represented by the aforementioned formula (a0-r-2) are shown below. * indicates the bonding site with the oxy group (—O—).

Specific examples of the structural unit (a0) are shown below. In the formulae shown below, R^(α) represents a hydrogen atom, a methyl group or a trifluoromethyl group.

Among the above examples, as the structural unit (a0), at least one member selected from the group consisting of structural units represented by chemical formula (a0-1a-u101), chemical formula (a0-1a-u103), chemical formula (a0-1a-u110) and chemical formula (a0-1a-u146) is preferable.

As the structural unit (a0) contained in the component (A1), 1 kind of structural unit may be used, or 2 or more kinds of structural units may be used.

In the component (A1), the amount of the structural unit (a0) based on the combined total (100 mol %) of all structural units constituting the component (A1) is preferably 20 to 80 mol %, more preferably 25 to 70 mol %, and still more preferably 30 to 60 mol %.

When the amount of the structural unit (a0) is at least as large as the lower limit of the above-mentioned preferable range, various lithography properties such as sensitivity, resolution and roughness may be improved. On the other hand, when the amount of the structural unit (a0) is no more than the upper limit of the above-mentioned range, a good balance may be achieved with the other structural units, and the lithography properties may be improved.

<<Other Structural Units>>

If desired, the component (A1) may include, in addition to the structural unit (a0), other structural unit.

Examples of the other structural unit include a structural unit (a10) containing a hydroxystyrene skeleton; a structural unit (a1) containing an acid decomposable group that exhibits increased polarity by the action of acid; a structural unit (a2) containing a lactone-containing cyclic group, an —SO₂— containing cyclic group or a carbonate-containing cyclic group; a structural unit (a3) containing a polar group-containing aliphatic hydrocarbon group; a structural unit (a9) represented by general formula (a9-1); a structural unit derived from styrene; a structural unit derived from a styrene derivative; and a structural unit containing an acid non-dissociable aliphatic cyclic group.

Structural Unit (a10):

The component (A1) preferably has, in addition to the structural unit (a1), a structural unit (a10) containing a hydroxystyrene skeleton.

Preferable examples of the structural unit (a10) include a structural unit represented by general formula (a10-1) shown below.

In the formula, R represents a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms; Ya^(x1) represents a single bond or a divalent linking group; Wa^(x1) represents an aromatic hydrocarbon group having a valency of (n_(ax1)+1); and n_(ax1) represents an integer of 1 to 3.

In general formula (a10-1), R represents a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms.

As the alkyl group of 1 to 5 carbon atoms for R, a linear or branched alkyl group of 1 to 5 carbon atoms is preferable, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group and a neopentyl group. The halogenated alkyl group of 1 to 5 carbon atoms represented by R is a group in which part or all of the hydrogen atoms of the aforementioned alkyl group of 1 to 5 carbon atoms have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable.

As R, a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and a hydrogen atom or a methyl group is particularly desirable in terms of industrial availability.

In formula (a10-1), Ya^(x1) represents a single bond or a divalent linking group. Preferable examples of the divalent linking group for Ya^(x1) include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom.

Divalent Hydrocarbon Group which May have a Substituent:

In the case where Ya^(x1) is a divalent linking group which may have a substituent, the hydrocarbon group may be either an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

Aliphatic Hydrocarbon Group for Ya^(x1)

The “aliphatic hydrocarbon group” refers to a hydrocarbon group that has no aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated. In general, the aliphatic hydrocarbon group is preferably saturated.

Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in the structure thereof can be given.

Linear or Branched Aliphatic Hydrocarbon Group

The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, still more preferably 1 to 4, and most preferably 1 to 3.

As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specific examples thereof include a methylene group [—CH₂—], an ethylene group [—(CH₂)₂—], a trimethylene group [—(CH₂)₃—], a tetramethylene group [—(CH₂)₄-] and a pentamethylene group [—(CH₂)₅—].

The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6, still more preferably 3 or 4, and most preferably 3.

As the branched aliphatic hydrocarbon group, branched alkylene groups are preferred, and specific examples include various alkylalkylene groups, including alkylmethylene groups such as —CH(CH₃)—, —CH(CH₂CH₃)—, —C(CH₃)₂—, —C(CH₃)(CH₂CH₃)—, —C(CH₃)(CH₂CH₂CH₃)—, and —C(CH₂CH₃)₂—; alkylethylene groups such as —CH(CH₃)CH₂—, —CH(CH₃)CH(CH₃)—, —C(CH₃)₂CH₂—, —CH(CH₂CH₃)CH₂—, and —C(CH₂CH₃)₂—CH₂—; alkyltrimethylene groups such as —CH(CH₃)CH₂CH₂—, and —CH₂CH(CH₃)CH₂—; and alkyltetramethylene groups such as —CH(CH₃)CH₂CH₂CH₂—, and —CH₂CH(CH₃)CH₂CH₂—. As the alkyl group within the alkylalkylene group, a linear alkyl group of 1 to 5 carbon atoms is preferable.

The linear or branched aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group of 1 to 5 carbon atoms, and a carbonyl group.

Aliphatic Hydrocarbon Group Containing a Ring in the Structure Thereof

As examples of the hydrocarbon group containing a ring in the structure thereof, a cyclic aliphatic hydrocarbon group containing a hetero atom in the ring structure thereof and may have a substituent (a group in which two hydrogen atoms have been removed from an aliphatic hydrocarbon ring), a group in which the cyclic aliphatic hydrocarbon group is bonded to the terminal of the aforementioned chain-like aliphatic hydrocarbon group, and a group in which the cyclic aliphatic group is interposed within the aforementioned linear or branched aliphatic hydrocarbon group, can be given. As the linear or branched aliphatic hydrocarbon group, the same groups as those described above can be used.

The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.

The cyclic aliphatic hydrocarbon group may be either a polycyclic group or a monocyclic group. As the monocyclic aliphatic hydrocarbon group, a group in which 2 hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. As the polycyclic group, a group in which 2 hydrogen atoms have been removed from a polycycloalkane is preferable, and the polycyclic group preferably has 7 to 12 carbon atoms. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane and tetracyclododecane.

The cyclic aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group and a carbonyl group.

The alkyl group as the substituent is preferably an alkyl group of 1 to 5 carbon atoms, and a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group is particularly desirable.

The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group or tert-butoxy group, and most preferably a methoxy group or an ethoxy group.

Examples of the halogen atom for the substituent include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.

Examples of the halogenated alkyl group for the substituent include groups in which part or all of the hydrogen atoms within the aforementioned alkyl groups has been substituted with the aforementioned halogen atoms.

The cyclic aliphatic hydrocarbon group may have part of the carbon atoms constituting the ring structure thereof substituted with a substituent containing a hetero atom. As the substituent containing a hetero atom, —O—, —C(═O)—O—, —S—, —S(═O)₂— or —S(═O)₂—O— is preferable.

Aromatic Hydrocarbon Group for Ya^(x1)

The aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring.

The aromatic ring is not particularly limited, as long as it is a cyclic conjugated compound having (4n+2)π electrons, and may be either monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, and still more preferably 6 to 15 carbon atoms, and most preferably 6 to 12 carbon atoms. Here, the number of carbon atoms within a substituent(s) is not included in the number of carbon atoms of the aromatic hydrocarbon group. Examples of the aromatic ring include aromatic hydrocarbon rings, such as benzene, naphthalene, anthracene and phenanthrene; and aromatic hetero rings in which part of the carbon atoms constituting the aforementioned aromatic hydrocarbon rings has been substituted with a hetero atom. Examples of the hetero atom within the aromatic hetero rings include an oxygen atom, a sulfur atom and a nitrogen atom. Specific examples of the aromatic hetero ring include a pyridine ring and a thiophene ring.

Specific examples of the aromatic hydrocarbon group include a group in which two hydrogen atoms have been removed from the aforementioned aromatic hydrocarbon ring or aromatic hetero ring (arylene group or heteroarylene group); a group in which two hydrogen atoms have been removed from an aromatic compound having two or more aromatic rings (biphenyl, fluorene or the like); and a group in which one hydrogen atom of the aforementioned aromatic hydrocarbon ring or aromatic hetero ring has been substituted with an alkylene group (a group in which one hydrogen atom has been removed from the aryl group within the aforementioned arylalkyl group such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, or a 2-naphthylethyl group, or a heteroarylalkyl group). The alkylene group which is bonded to the aforementioned aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 or 2 carbon atoms, and most preferably 1 carbon atom.

With respect to the aromatic hydrocarbon group, the hydrogen atom within the aromatic hydrocarbon group may be substituted with a substituent. For example, the hydrogen atom bonded to the aromatic ring within the aromatic hydrocarbon group may be substituted with a substituent. Examples of substituents include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxyl group.

The alkyl group as the substituent is preferably an alkyl group of 1 to 5 carbon atoms, and a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group is particularly desirable.

As the alkoxy group, the halogen atom and the halogenated alkyl group for the substituent, the same groups as the aforementioned substituent groups for substituting a hydrogen atom within the cyclic aliphatic hydrocarbon group can be used.

Divalent Linking Group Containing a Hetero Atom

In the case where Ya^(x1) represents a divalent linking group containing a hetero atom, preferable examples of the linking group include —O—, —C(═O)—O—, —C(═O)—, —O—C(═O)—O—, —C(═O)—NH—, —NH—, —NH—C(═NH)— (may be substituted with a substituent such as an alkyl group, an acyl group or the like), —S—, —S(═O)₂—, —S(═O)₂—O—, and a group represented by general formula: —Y²¹—O—Y²²—, —Y²¹—O—, —Y²¹—C(═O)—O—, —C(═O)—O—Y²¹—, —[Y²¹—C(═O)—O]_(m″)—Y²²—, —Y²¹—O—C(═O)—Y²²— or —Y²¹—S(═O)₂—O—Y²²— [in the formulae, Y²¹ and Y²² each independently represents a divalent hydrocarbon group which may have a substituent, O represents an oxygen atom, and m′ represents an integer of 0 to 3].

In the case where the divalent linking group containing a hetero atom is —C(═O)—NH—, —C(═O)—NH—C(═O)—, —NH— or —NH—C(═NH)—, H may be substituted with a substituent such as an alkyl group, an acyl group or the like. The substituent (an alkyl group, an acyl group or the like) preferably has 1 to 10 carbon atoms, more preferably 1 to 8, and most preferably 1 to 5.

In general formulae —Y²¹—O—Y²²—, —Y²¹—O—, —Y²¹—C(═O)—O—, —C(═O)—O—Y²¹—, —[Y²¹—C(═O)—O]_(m″)—Y²²—, —Y²¹—O—C(═O)—Y²²— or —Y²¹—S(═O)₂—O—Y²²—, Y²¹ and Y²² each independently represents a divalent hydrocarbon group which may have a substituent. Examples of the divalent hydrocarbon group include the same groups as those described above as the “divalent hydrocarbon group which may have a substituent” in the explanation of the aforementioned divalent linking group.

As Y²¹, a linear aliphatic hydrocarbon group is preferable, more preferably a linear alkylene group, still more preferably a linear alkylene group of 1 to 5 carbon atoms, and a methylene group or an ethylene group is particularly desirable.

As Y²², a linear or branched aliphatic hydrocarbon group is preferable, and a methylene group, an ethylene group or an alkylmethylene group is more preferable. The alkyl group within the alkylmethylene group is preferably a linear alkyl group of 1 to 5 carbon atoms, more preferably a linear alkyl group of 1 to 3 carbon atoms, and most preferably a methyl group.

In the group represented by the formula —[Y²¹—C(═O)—O]_(m″)—Y²²—, m″ represents an integer of 0 to 3, preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 1. Namely, it is particularly desirable that the group represented by the formula —[Y²¹—C(═O)—O]_(m″)—Y²²— is a group represented by the formula —Y²¹—C(═O)—O—Y²²—. Among these, a group represented by the formula —(CH₂)_(a′)—C(═O)—O—(CH₂)_(b′)— is preferable. In the formula, a′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, still more preferably 1 or 2, and most preferably 1. b′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, still more preferably 1 or 2, and most preferably 1.

Ya^(x1) preferably represents an ester bond [—C(═O)—O—], an ether bond (—O—), —C(═O)—NH—, a linear or branched alkylene group, a combination of these, or a single bond, and more preferably a single bond.

In formula (a10-1), Wa^(x1) represents an aromatic hydrocarbon group having a valency of (n_(ax1)+1).

Examples of the aromatic hydrocarbon group for Wa^(x1) include a group obtained by removing (n_(ax1)+1)hydrogen atoms from an aromatic ring. The aromatic ring is not particularly limited, as long as it is a cyclic conjugated compound having (4n+2)π electrons, and may be either monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, and still more preferably 6 to 15 carbon atoms, and most preferably 6 to 12 carbon atoms. Examples of the aromatic ring include aromatic hydrocarbon rings, such as benzene, naphthalene, anthracene and phenanthrene; and aromatic hetero rings in which part of the carbon atoms constituting the aforementioned aromatic hydrocarbon rings has been substituted with a hetero atom. Examples of the hetero atom within the aromatic hetero rings include an oxygen atom, a sulfur atom and a nitrogen atom. Specific examples of the aromatic hetero ring include a pyridine ring and a thiophene ring.

In formula (a10-1), n_(ax1) is an integer of 1 to 3, preferably 1 or 2, and more preferably 1.

Specific examples of the structural unit represented by general formula (a10-1) are shown below.

In the following formulae, R^(α) represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a10) contained in the component (A1), 1 kind of structural unit may be used, or 2 or more kinds may be used.

In the component (A1), the amount of the structural unit (a10) based on the combined total (100 mol %) of all structural units constituting the component (A1) is, for example, 0 to 80 mol %, preferably 10 to 80 mol %, more preferably 20 to 70 mol %, and still more preferably 20 to 60 mol %.

When the amount of the structural unit (a10) is at least as large as the lower limit of the above-mentioned preferable range, various lithography properties such as sensitivity, resolution and roughness may be improved. On the other hand, when the amount of the structural unit (a10) is no more than the upper limit of the above-mentioned preferable range, a good balance may be achieved with the other structural units, and the lithography properties may be improved.

Structural Unit (a1):

In addition to the structural unit (a0), the component (A1) may include a structural unit (a1) containing an acid decomposable group that exhibits increased polarity by the action of acid (provided that structural units which fall under the definition of the structural unit (a0) is excluded).

The term “acid decomposable group” refers to a group in which at least a part of the bond within the structure thereof is cleaved by the action of an acid.

Examples of acid decomposable groups which exhibit increased polarity by the action of an acid include groups which are decomposed by the action of an acid to form a polar group.

Examples of the polar group include a carboxy group, a hydroxy group, an amino group and a sulfo group (—SO₃H). Among these, a polar group containing —OH in the structure thereof (hereafter, referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxy group is more preferable, and a carboxy group is particularly desirable.

More specifically, as an example of an acid decomposable group, a group in which the aforementioned polar group has been protected with an acid dissociable group (such as a group in which the hydrogen atom of the OH-containing polar group has been protected with an acid dissociable group) can be given.

The “acid dissociable group” refers to both (i) a group in which the bond between the acid dissociable group and the adjacent atom is cleaved by the action of acid; and (ii) a group in which one of the bonds is cleaved by the action of acid, and then a decarboxylation reaction occurs, thereby cleaving the bond between the acid dissociable group and the adjacent atom.

It is necessary that the acid dissociable group that constitutes the acid decomposable group is a group which exhibits a lower polarity than the polar group generated by the dissociation of the acid dissociable group. Thus, when the acid dissociable group is dissociated by the action of acid, a polar group exhibiting a higher polarity than that of the acid dissociable group is generated, thereby increasing the polarity. As a result, the polarity of the entire component (A1) is increased. By the increase in the polarity, the solubility in an alkali developing solution changes, and the solubility in an alkali developing solution is relatively increased, whereas the solubility in an organic developing solution is relatively decreased.

Examples of the acid dissociable group for the structural unit (a1) include acid dissociable groups which have been proposed for a base resin of a chemically amplified resist composition, provided that the acid dissociable group “—C^(t)(R¹¹)(R¹²)(R¹³)” in the aforementioned general formula (a0-1) is excluded.

Specific examples of acid dissociable groups for the base resin of a conventional chemically amplified resist include “acetal-type acid dissociable group”, “tertiary alkyl ester-type acid dissociable group” and “tertiary alkyloxycarbonyl acid dissociable group” described below.

Acetal-Type Acid Dissociable Group

Examples of the acid dissociable group for protecting the carboxy group or hydroxy group as a polar group include the acid dissociable group represented by general formula (a1-r-1) shown below (hereafter, referred to as “acetal-type acid dissociable group”).

In the formula, Ra′¹ and Ra′² represents a hydrogen atom or an alkyl group; and Ra′³ represents a hydrocarbon group, provided that Ra′³ may be bonded to Ra′¹ or Ra′².

In the formula (a1-r-1), it is preferable that at least one of Ra′¹ and Ra′² represents a hydrogen atom, and it is more preferable that both of Ra′¹ and Ra′² represent a hydrogen atom.

In the case where Ra′¹ or Ra′² is an alkyl group, as the alkyl group, the same alkyl groups as those described above the for the substituent which may be bonded to the carbon atom on the α-position of the aforementioned α-substituted acrylate ester can be mentioned, and an alkyl group of 1 to 5 carbon atoms is preferable. Specific examples include linear or branched alkyl groups. Specific examples of the alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group and a neopentyl group. Of these, a methyl group or an ethyl group is preferable, and a methyl group is particularly preferable.

In formula (a1-r-1), examples of the hydrocarbon group for Ra′³ include a linear or branched alkyl group and a cyclic hydrocarbon group.

The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group and an n-pentyl group. Among these, a methyl group, an ethyl group or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.

The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5. Specific examples include an isopropyl group, an isobutyl group, a tert-butyl group, an isopentyl group, a neopentyl group a 1,1-diethylpropyl group and a 2,2-dimethylbutyl group. Among these, an isopropyl group is preferable.

In the case where Ra′³ represents a cyclic hydrocarbon group, the cyclic hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be polycyclic or monocyclic.

As the monocyclic aliphatic hydrocarbon group, a group in which 1 hydrogen atom has been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane.

As the polycyclic aliphatic hydrocarbon group, a group in which 1 hydrogen atom has been removed from a polycycloalkane is preferable, and the polycyclic group preferably has 7 to 12 carbon atoms. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane and tetracyclododecane.

When the monovalent hydrocarbon group for Ra′³ is an aromatic hydrocarbon group, the aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring.

The aromatic ring is not particularly limited, as long as it is a cyclic conjugated compound having (4n+2)π electrons, and may be either monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20, still more preferably 6 to 15, and most preferably 6 to 12. Examples of the aromatic ring include aromatic hydrocarbon rings, such as benzene, naphthalene, anthracene and phenanthrene; and aromatic hetero rings in which part of the carbon atoms constituting the aforementioned aromatic hydrocarbon rings has been substituted with a hetero atom. Examples of the hetero atom within the aromatic hetero rings include an oxygen atom, a sulfur atom and a nitrogen atom. Specific examples of the aromatic hetero ring include a pyridine ring and a thiophene ring.

Specific examples of the aromatic hydrocarbon group for Ra′³ include a group in which one hydrogen atom has been removed from the aforementioned aromatic hydrocarbon ring or aromatic hetero ring (aryl group or heteroaryl group); a group in which one hydrogen atom has been removed from an aromatic compound having two or more aromatic rings (biphenyl, fluorene or the like); and a group in which one hydrogen atom of the aforementioned aromatic hydrocarbon ring or aromatic hetero ring has been substituted with an alkylene group (an arylalkyl group such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, or a 2-naphthylethyl group). The alkylene group bonded to the aforementioned aromatic hydrocarbon ring or the aromatic hetero ring preferably has 1 to 4 carbon atoms, more preferably 1 or 2 carbon atoms, and most preferably 1 carbon atom.

In the case where Ra′³ is bonded to Ra′¹ or Ra′² to form a ring, the cyclic group is preferably a 4 to 7-membered ring, and more preferably a 4 to 6-membered ring. Specific examples of the cyclic group include tetrahydropyranyl group and tetrahydrofuranyl group.

Tertiary Alkyl Ester-Type Acid Dissociable Group

Examples of the acid dissociable group for protecting the carboxy group as a polar group include the acid dissociable group represented by general formula (a1-r-2) shown below. Among the acid dissociable groups represented by general formula (a1-r-2), for convenience, a group which is constituted of alkyl groups is referred to as “tertiary ester-type acid dissociable group”.

In the formula, Ra′⁴ to Ra′⁶ each independently represents a hydrocarbon group, provided that Ra′⁵ and Ra′⁶ may be mutually bonded to form a ring.

As the hydrocarbon group for Ra′⁴ to Ra′⁶, the same groups as those described above for Ra′³ can be mentioned.

Ra′⁴ is preferably an alkyl group of 1 to 5 carbon atoms. In the case where Ra′⁵ and Ra′⁶ are mutually bonded to form a ring, a group represented by general formula (a1-r2-1) shown below can be mentioned. On the other hand, in the case where Ra′⁴ to Ra′⁶ are not mutually bonded and independently represent a hydrocarbon group, the group represented by general formula (a1-r2-2) shown below can be mentioned.

In the formulae, Ra′¹⁰ represents an alkyl group of 1 to 10 carbon atoms; Ra′¹¹ is a group which forms an aliphatic cyclic group together with a carbon atom having Ra′¹⁰ bonded thereto; and Ra′¹² to Ra′¹⁴ each independently represents a hydrocarbon group.

In the formula (a1-r2-1), as the alkyl group of 1 to 10 carbon atoms for Ra′¹⁰ the same groups as described above for the linear or branched alkyl group for Ra′³ in the formula (a1-r-1) are preferable. In the formula (a1-r2-1), as the aliphatic cyclic group which is formed by Ra′¹¹ together with the carbon atom bonded to Ra′¹⁰, the same groups as those described above for the monocyclic or polycyclic aliphatic hydrocarbon group for Ra′³ in the formula (a1-r-1) are preferable.

In the formula (a1-r2-2), it is preferable that Ra′¹² and Ra′¹⁴ each independently represents an alkyl group or 1 to 10 carbon atoms, and it is more preferable that the alkyl group is the same group as the described above for the linear or branched alkyl group for Ra′³ in the formula (a1-r-1), it is still more preferable that the alkyl group is a linear alkyl group of 1 to 5 carbon atoms, and it is particularly preferable that the alkyl group is a methyl group or an ethyl group.

In the formula (a1-r2-2), it is preferable that Ra′¹³ is the same group as described above for the linear or branched alkyl group or monocyclic or polycyclic alicyclic hydrocarbon group for Ra′³ in the formula (a1-r-1). Among these examples, monocyclic or polycyclic aliphatic hydrocarbon group for Ra′³ are more preferable.

Specific examples of the group represented by the aforementioned formula (a1-r2-1) are shown below. and * represents a valence bond.

Specific examples of the group represented by the aforementioned formula (a1-r2-2) are shown below.

Tertiary Alkyloxycarbonyl Acid Dissociable Group

Examples of the acid dissociable group for protecting a hydroxy group as a polar group include the acid dissociable group represented by general formula (a1-r-3) shown below (hereafter, for convenience, referred to as “tertiary alkyloxycarbonyl-type acid dissociable group”).

In the formula, Ra′⁷ to Ra′⁹ each independently represents an alkyl group.

In formula (a1-r-3), each of Ra′⁷ to Ra′⁹ is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably an alkyl group having 1 to 3 carbon atoms.

Further, the total number of carbon atoms within the alkyl group is preferably 3 to 7, more preferably 3 to 5, and most preferably 3 or 4.

Examples of the structural unit (a1) include a structural unit derived from an acrylate ester which may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent; a structural unit derived from an acrylamide; a structural unit derived from hydroxystyrene or a hydroxystyrene derivative in which at least a part of the hydrogen atom of the hydroxy group is protected with a substituent containing an acid decomposable group; and a structural unit derived from vinylbenzoic acid or a vinylbenzoic acid derivative in which at least a part of the hydrogen atom within —C(═O)—OH is protected with a substituent containing an acid decomposable group.

As the structural unit (a1), a structural unit derived from an acrylate ester which may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent is preferable.

Specific examples of preferable structural units for the structural unit (a1) include structural units represented by general formula (a1-1) or (a1-2) shown below.

In the formula, R represents a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms; Va¹ represents a divalent hydrocarbon group optionally having an ether bond; n_(a1) represents an integer of 0 to 2; Ra¹ represents an acid dissociable group represented by the aforementioned formula (a1-r-1) or (a1-r-2); Wa¹ represents a hydrocarbon group having a valency of n_(a2)+1; n_(a2) represents an integer of 1 to 3; Ra² represents an acid dissociable group represented by the aforementioned formula (a1-r-1) or (a1-r-3).

In the aforementioned formula (a1-1), as the alkyl group of 1 to 5 carbon atoms for R, a linear or branched alkyl group of 1 to 5 carbon atoms is preferable, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group and a neopentyl group. The halogenated alkyl group of 1 to 5 carbon atoms represented by R is a group in which part or all of the hydrogen atoms of the aforementioned alkyl group of 1 to 5 carbon atoms have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable.

As R, a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and a hydrogen atom or a methyl group is particularly desirable in terms of industrial availability.

In formula (a1-1), the divalent linking group for Va¹ is the same as defined for the divalent linking group for Ya^(x0) described above in relation to W¹ in the aforementioned formula (a0-1).

In the aforementioned formula (a1-2), the hydrocarbon group for Wa¹ having a valency of n_(a2)+1 may be either an aliphatic hydrocarbon group or an aromatic hydrocarbon group. The aliphatic cyclic group refers to a hydrocarbon group that has no aromaticity, and may be either saturated or unsaturated, but is preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure thereof, and a combination of the linear or branched aliphatic hydrocarbon group and the aliphatic hydrocarbon group containing a ring in the structure thereof.

The valency of n_(a2)+1 is preferably divalent, trivalent or tetravalent, and divalent or trivalent is more preferable.

Specific examples of structural unit represented by formula (a1-1) are shown below. In the formulae shown below, R^(α) represents a hydrogen atom, a methyl group or a trifluoromethyl group.

Specific examples of structural unit represented by formula (a1-2) are shown below.

As the structural unit (a1) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.

When the component (A1) includes the structural unit (a1), the amount of the structural unit (a1) based on the combined total of all structural units constituting the component (A1) (100 mol %) is preferably 1 to 50 mol %, more preferably 5 to 45 mol %, and still more preferably 5 to 30 mol %.

When the amount of the structural unit (a1) is at least as large as the lower limit of the above-mentioned range, a resist pattern can be reliably obtained, and the sensitivity, resolution, roughness and various lithography properties such as EL margin are further improved. On the other hand, when the amount of the structural unit (a1) is no more than the upper limit of the above-mentioned range, a good balance can be achieved with the other structural units.

Structural Unit (a2):

The component (A1) may include, in addition to the structural unit (a0), a structural unit (a2) containing a lactone-containing cyclic group, an —SO₂— containing cyclic group or a carbonate-containing cyclic group (provided that structural units which fall under the definition of the structural unit (a0) or the structural unit (a1) are excluded).

When the component (A1) is used for forming a resist film, the lactone-containing cyclic group, the —SO₂— containing cyclic group or the carbonate-containing cyclic group within the structural unit (a2) is effective in improving the adhesion between the resist film and the substrate. In addition, by virtue of containing the structural unit (a2), for example, the acid diffusion length is appropriately adjusted, the adhesion of the resist film to the substrate is enhanced, or the solubility during development is appropriately adjusted. As a result, the lithography properties are enhanced.

The term “lactone-containing cyclic group” refers to a cyclic group including a ring containing a —O—C(═O)— structure (lactone ring). The term “lactone ring” refers to a single ring containing a —O—C(O)— structure, and this ring is counted as the first ring. A lactone-containing cyclic group in which the only ring structure is the lactone ring is referred to as a monocyclic group, and groups containing other ring structures are described as polycyclic groups regardless of the structure of the other rings. The lactone-containing cyclic group may be either a monocyclic group or a polycyclic group.

The lactone-containing cyclic group for the structural unit (a2) is not particularly limited, and an arbitrary structural unit may be used. Specific examples include groups represented by general formulae (a2-r-1) to (a2-r-7) shown below.

In the formulae, each Ra′²¹ independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxy group, —COOR″, —OC(═O)R″, a hydroxyalkyl group or a cyano group; R″ represents a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group or an —SO₂— containing cyclic group; A″ represents an oxygen atom (—O—), a sulfur atom (—S—) or an alkylene group of 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom; n′ represents an integer of 0 to 2; and m′ represents 0 or 1.

In formulae (a2-r-1) to (a2-r-7), the alkyl group for Ra′²¹ is preferably an alkyl group of 1 to 6 carbon atoms. Further, the alkyl group is preferably a linear alkyl group or a branched alkyl group. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group and a hexyl group. Among these, a methyl group or ethyl group is preferable, and a methyl group is particularly desirable.

The alkoxy group for Ra′²¹ is preferably an alkoxy group of 1 to 6 carbon atoms.

Further, the alkoxy group is preferably a linear or branched alkoxy group. Specific examples of the alkoxy groups include the aforementioned alkyl groups for Ra′²¹ having an oxygen atom (—O—) bonded thereto.

As examples of the halogen atom for Ra′²¹, a fluorine atom, chlorine atom, bromine atom and iodine atom can be given. Among these, a fluorine atom is preferable.

Examples of the halogenated alkyl group for Ra′²¹ include groups in which part or all of the hydrogen atoms within the aforementioned alkyl group for Ra′²¹ has been substituted with the aforementioned halogen atoms. As the halogenated alkyl group, a fluorinated alkyl group is preferable, and a perfluoroalkyl group is particularly desirable.

With respect to —COOR″ and —OC(═O)R″ for Ra′²¹, R″ represents a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group or an —SO₂— containing cyclic group.

The alkyl group for R″ may be linear, branched or cyclic, and preferably has 1 to 15 carbon atoms.

When R″ represents a linear or branched alkyl group, it is preferably an alkyl group of 1 to 10 carbon atoms, more preferably an alkyl group of 1 to 5 carbon atoms, and most preferably a methyl group or an ethyl group.

When R″ is a cyclic alkyl group (cycloalkyl group), it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane or a polycycloalkane such as a bicycloalkane, tricycloalkane or tetracycloalkane which may or may not be substituted with a fluorine atom or a fluorinated alkyl group. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; and groups in which one or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane.

Examples of the lactone-containing cyclic group for R″ include groups represented by the aforementioned general formulae (a2-r-1) to (a2-r-7). The carbonate-containing cyclic group for R″ is the same as defined for the carbonate-containing cyclic group described later. Specific examples of the carbonate-containing cyclic group include groups represented by general formulae (ax3-r-1) to (ax3-r-3).

The —SO₂— containing cyclic group for R″ is the same as defined for the —SO₂— containing cyclic group described later. Specific examples of the —SO₂— containing cyclic group include groups represented by general formulae (a5-r-1) to (a5-r-4). The hydroxyalkyl group for Ra′²¹ preferably has 1 to 6 carbon atoms, and specific examples thereof include the alkyl groups for Ra′²¹ in which at least one hydrogen atom has been substituted with a hydroxy group.

In formulae (a2-r-2), (a2-r-3) and (a2-r-5), as the alkylene group of 1 to 5 carbon atoms represented by A″, a linear or branched alkylene group is preferable, and examples thereof include a methylene group, an ethylene group, an n-propylene group and an isopropylene group. Examples of alkylene groups that contain an oxygen atom or a sulfur atom include the aforementioned alkylene groups in which —O— or —S— is bonded to the terminal of the alkylene group or present between the carbon atoms of the alkylene group. Specific examples of such alkylene groups include —O—CH₂—, —CH₂—O—CH₂—, —S—CH₂— and —CH₂—S—CH₂—. As A″, an alkylene group of 1 to 5 carbon atoms or —O— is preferable, more preferably an alkylene group of 1 to 5 carbon atoms, and most preferably a methylene group.

Specific examples of the groups represented by the aforementioned general formulae (a2-r-1) to (a2-r-7) are shown below.

An “—SO₂— containing cyclic group” refers to a cyclic group having a ring containing —SO₂— within the ring structure thereof, i.e., a cyclic group in which the sulfur atom (S) within —SO₂— forms part of the ring skeleton of the cyclic group. The ring containing —SO₂— within the ring skeleton thereof is counted as the first ring. A cyclic group in which the only ring structure is the ring that contains —SO₂— in the ring skeleton thereof is referred to as a monocyclic group, and a group containing other ring structures is described as a polycyclic group regardless of the structure of the other rings. The —SO₂— containing cyclic group may be either a monocyclic group or a polycyclic group. As the —SO₂— containing cyclic group, a cyclic group containing —O—SO₂— within the ring skeleton thereof, i.e., a cyclic group containing a sultone ring in which —O—S— within the —O—SO₂— group forms part of the ring skeleton thereof is particularly desirable. More specific examples of the —SO₂— containing cyclic group include groups represented by general formulas (a5-r-1) to (a5-r-4) shown below.

In the formulae, each Ra′⁵¹ independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxy group, —COOR″, —OC(═O)R″, a hydroxyalkyl group or a cyano group; R″ represents a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group or an —SO₂— containing cyclic group; A″ represents an oxygen atom, a sulfur atom or an alkylene group of 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom; and n′ represents an integer of 0 to 2.

In general formulae (a5-r-1) and (a5-r-2), A″ is the same as defined for A″ in general formulae (a2-r-2), (a2-r-3) and (a2-r-5).

Examples of the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR″, —OC(═O)R″ and hydroxyalkyl group for Ra′⁵¹ include the same groups as those described above in the explanation of Ra′²¹ in the general formulas (a2-r-1) to (a2-r-7).

Specific examples of the groups represented by the aforementioned general formulae (a5-r-1) to (a5-r-4) are shown below. In the formulae shown below, “Ac” represents an acetyl group.

The term “carbonate-containing cyclic group” refers to a cyclic group including a ring containing a —O—C(═O)—O— structure (carbonate ring). The term “carbonate ring” refers to a single ring containing a —O—C(═O)—O— structure, and this ring is counted as the first ring. A carbonate-containing cyclic group in which the only ring structure is the carbonate ring is referred to as a monocyclic group, and groups containing other ring structures are described as polycyclic groups regardless of the structure of the other rings. The carbonate-containing cyclic group may be either a monocyclic group or a polycyclic group.

The carbonate-containing cyclic group is not particularly limited, and an arbitrary group may be used. Specific examples include groups represented by general formulae (ax3-r-1) to (ax3-r-3) shown below.

In the formulae, each Ra′^(x31) independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxy group, —COOR″, —OC(═O)R″, a hydroxyalkyl group or a cyano group; R″ represents a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group or an —SO₂— containing cyclic group; A″ represents an oxygen atom, a sulfur atom or an alkylene group of 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom; p′ represents an integer of 0 to 3; and q′ represents 0 or 1.

In general formulae (ax3-r-2) and (ax3-r-3), A″ is the same as defined for A″ in general formulae (a2-r-2), (a2-r-3) and (a2-r-5).

Examples of the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR″, —OC(═O)R″ and hydroxyalkyl group for Ra′³¹ include the same groups as those described above in the explanation of Ra′²¹ in the general formulas (a2-r-1) to (a2-r-7).

Specific examples of the groups represented by the aforementioned general formulae (ax3-r-1) to (ax3-r-3) are shown below.

As the structural unit (a2), a structural unit derived from an acrylate ester which may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent is preferable.

The structural unit (a2) is preferably a structural unit represented by general formula (a2-1) shown below.

In the formula, R represents a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms; Ya²¹ represents a single bond or a divalent linking group; La²¹ represents —O—, —COO—, —CON(R′)—, —OCO—, —CONHCO— or —CONHCS—; and R′ represents a hydrogen atom or a methyl group; provided that, when La²¹ represents —O—, Ya²¹ does not represents —CO—; and Ra²¹ represents a lactone-containing cyclic group, a carbonate-containing cyclic group or an —SO₂— containing cyclic group.

In the formula (a2-1), R is the same as defined above. As R, a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and a hydrogen atom or a methyl group is particularly desirable in terms of industrial availability.

In the formula (a2-1), the divalent linking group for Ya²¹ is not particularly limited, and preferable examples thereof include a divalent hydrocarbon group which may have a substituent and a divalent linking group containing a hetero atom. As the divalent linking group which may have a substituent or the divalent linking group containing a hetero atom for Ya²¹, the same divalent linking groups (divalent linking group which may have a substituent or divalent linking group containing a hetero atom) described above for Ya^(x0) may be mentioned.

Ya²¹ preferably represents an ester bond [—C(═O)—O—], an ether bond (—O—), a linear or branched alkylene group, a combination of these, or a single bond.

In the formula (a2-1), Ra²¹ represents a lactone-containing cyclic group, an —SO₂— containing cyclic group or a carbonate-containing cyclic group.

Preferable examples of the lactone-containing cyclic group, the —SO₂— containing cyclic group and the carbonate-containing cyclic group for Ra²¹ include groups represented by general formulae (a2-r-1) to (a2-r-7), groups represented by general formulae (a5-r-1) to (a5-r-4) and groups represented by general formulae (ax3-r-1) to (ax3-r-3).

Among the above examples, a lactone-containing cyclic group or a —SO₂— containing cyclic group is preferable, and a group represented by general formula (a2-r-1), (a2-r-2), (a2-r-6) or (a5-r-1) is more preferable. Specifically, a group represented by any of chemical formulae (r-lc-1-1) to (r-lc-1-7), (r-lc-2-1) to (r-lc-2-18), (r-lc-6-1), (r-sl-1-1) and (r-sl-1-18) is still more preferable.

As the structural unit (a2) contained in the component (A1), 1 kind of structural unit may be used, or 2 or more kinds may be used.

When the component (A1) includes the structural unit (a2), the amount of the structural unit (a2) based on the combined total (100 mol %) of all structural units constituting the component (A1) is preferably 10 to 80 mol %, more preferably 30 to 70 mol %, and still more preferably 35 to 60 mol %.

When the amount of the structural unit (a2) is at least as large as the lower limit of the above preferable range, the effect of using the structural unit (a2) may be satisfactorily achieved due to the aforementioned effects. On the other hand, when the amount of the structural unit (a2) is no more than the upper limit of the above preferable range, a good balance may be achieved with the other structural units, and various lithography properties may be improved.

Structural Unit (a3):

The component (A1) may include, in addition to the structural unit (a0), a structural unit (a3) containing a polar group-containing aliphatic hydrocarbon group (provided that the structural units that fall under the definition of structural units (a0), (a1) or (a2) are excluded). When the component (A1) includes the structural unit (a3), the hydrophilicity of the component (A1) is enhanced, thereby contributing to improvement in resolution. Further, the acid diffusion length may be appropriately adjusted.

Examples of the polar group include a hydroxyl group, cyano group, carboxyl group, or hydroxyalkyl group in which part of the hydrogen atoms of the alkyl group have been substituted with fluorine atoms, although a hydroxyl group is particularly desirable.

Examples of the aliphatic hydrocarbon group include linear or branched hydrocarbon groups (preferably alkylene groups) of 1 to 10 carbon atoms, and cyclic aliphatic hydrocarbon groups (cyclic groups). These cyclic groups can be selected appropriately from the multitude of groups that have been proposed for the resins of resist compositions designed for use with ArF excimer lasers.

In the case where the cyclic group is a monocyclic group, the monocyclic group preferably has 3 to 10 carbon atoms. Of the various possibilities, structural units derived from an acrylate ester that include an aliphatic monocyclic group that contains a hydroxyl group, cyano group, carboxyl group or a hydroxyalkyl group in which part of the hydrogen atoms of the alkyl group have been substituted with fluorine atoms are particularly desirable. Examples of the monocyclic groups include groups in which two or more hydrogen atoms have been removed from a monocycloalkane. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane, cyclohexane or cyclooctane. Of these polycyclic groups, groups in which two or more hydrogen atoms have been removed from cyclopentane or cyclohexane are preferred industrially.

In the case where the cyclic group is a polycyclic group, the polycyclic group preferably has 7 to 30 carbon atoms. Of the various possibilities, structural units derived from an acrylate ester that include an aliphatic polycyclic group that contains a hydroxyl group, cyano group, carboxyl group or a hydroxyalkyl group in which part of the hydrogen atoms of the alkyl group have been substituted with fluorine atoms are particularly desirable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from a bicycloalkane, tricycloalkane, tetracycloalkane or the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane. Of these polycyclic groups, groups in which two or more hydrogen atoms have been removed from adamantane, norbornane or tetracyclododecane are preferred industrially.

As the structural unit (a3), there is no particular limitation as long as it is a structural unit containing a polar group-containing aliphatic hydrocarbon group, and an arbitrary structural unit may be used.

The structural unit (a3) is preferably a structural unit derived from an acrylate ester which may have the hydrogen atom bonded to the carbon atom on the α-position substituted with a substituent and contains a polar group-containing aliphatic hydrocarbon group.

When the aliphatic hydrocarbon group within the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group of 1 to 10 carbon atoms, the structural unit (a3) is preferably a structural unit derived from a hydroxyethyl ester of acrylic acid.

On the other hand, in the structural unit (a3), when the hydrocarbon group within the polar group-containing aliphatic hydrocarbon group is a polycyclic group, structural units represented by formulas (a3-1), (a3-2), (a3-3) and (a3-4) shown below are preferable.

In the formulas, R is the same as defined above; j is an integer of 1 to 3; k is an integer of 1 to 3; t′ is an integer of 1 to 3; 1 is an integer of 0 to 5; and s is an integer of 1 to 3.

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl groups be bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group be bonded to the 3rd position of the adamantyl group.

j is preferably 1, and it is particularly desirable that the hydroxyl group be bonded to the 3rd position of the adamantyl group.

In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.

In formula (a3-3), t′ is preferably 1. l is preferably 1. s is preferably 1. Further, it is preferable that a 2-norbornyl group or 3-norbornyl group be bonded to the terminal of the carboxy group of the acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

In formula (a3-4), t′ is preferably 1 or 2. l is preferably 0 or 1. s is preferably 1. The fluorinated alkyl alcohol is preferably bonded to the 3rd or 5th position of the cyclohexyl group.

As the structural unit (a3) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.

When the component (A1) contains the structural unit (a3), the amount of the structural unit (a3) within the component (A1) based on the combined total (100 mol %) of all structural units constituting the component (A1) is preferably 1 to 30 mol %, more preferably 2 to 25 mol %, and still more preferably 5 to 20 mol %.

When the amount of the structural unit (a3) is at least as large as the lower limit of the above preferable range, the effect of using the structural unit (a3) may be satisfactorily achieved due to the aforementioned effects. On the other hand, when the amount of the structural unit (a3) is no more than the upper limit of the above preferable range, a good balance may be achieved with the other structural units, and various lithography properties may be improved.

Structural Unit (a9):

The component (A1) may include, in addition to the structural unit (a0), a structural unit (a9) represented by general formula (a9-1) shown below.

In the formula, R represents a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms; Ya⁹¹ represents a single bond or a divalent linking group; Ya⁹² represents a divalent linking group; and R⁹¹ represents a hydrocarbon group which may have a substituent.

In the general formula (a9-1), R is the same as defined above.

As R, a hydrogen atom, an alkyl group of 1 to 5 carbon atoms or a fluorinated alkyl group of 1 to 5 carbon atoms is preferable, and a hydrogen atom or a methyl group is particularly desirable in terms of industrial availability.

In formula (a9-1), the divalent linking group for Ya⁹¹ is the same as defined for the divalent linking group (divalent hydrocarbon group which may have a substituent, a divalent linking group containing a hetero atom) for Ya^(x0) described above. Among these, Ya⁹¹ is preferably a single bond.

In formula (a9-1), the divalent linking group for Ya⁹² is the same as defined for the divalent linking group (divalent hydrocarbon group which may have a substituent, a divalent linking group containing a hetero atom) for Ya^(x0) described above.

With respect to the divalent linking group for Ya⁹², as the divalent hydrocarbon group which may have a substituent, a linear or branched aliphatic hydrocarbon group is preferable.

In the case where Ya⁹² represents a divalent linking group containing a hetero atom, examples of the linking group include —O—, —C(═O)—O—, —C(═O)—, —O—C(═O)—O—, —C(═O)—NH—, —NH—, —NH—C(═NH)— (wherein H may be substituted with a substituent such as an alkyl group or an acyl group), —S—, —S(═O)₂—, —S(═O)₂—O—, C(═S), a group represented by general formula —Y²¹—O—Y²²—, —Y²¹—O—, —Y²¹—C(═O)—O—, —C(═O)—O—Y²¹, —[Y²¹—C(═O)—O]_(m′)—Y²²— or —Y²¹—O—C(═O)—Y²²— [in the formulae, Y²¹ and Y²² each independently represents a divalent hydrocarbon group which may have a substituent, and O represents an oxygen atom; and m′ represents an integer of 0 to 3. Among these examples, —C(═O)— and —C(═S)— are preferable.

In general formula (a9-1), examples of the hydrocarbon group for R⁹¹ include an alkyl group, a monovalent alicyclic hydrocarbon group, an aryl group and an aralkyl group.

The alkyl group for R⁹¹ preferably has 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms, and still more preferably 1 to 4 carbon atoms. The alkyl group may be linear or branched. Specific examples of preferable alkyl groups include a methyl group, an ethyl group, a propyl group, a butyl group, a hexyl group and an octyl group.

The monovalent alicyclic hydrocarbon group for R⁹¹ preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms. The monovalent alicyclic hydrocarbon group may be polycyclic or monocyclic. As the monocyclic alicyclic hydrocarbon group, a group in which one or more hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclobutane, cyclopentane and cyclohexane. As the polycyclic alicyclic hydrocarbon group, a group in which one or more hydrogen atoms have been removed from a polycycloalkane is preferable, and the polycyclic group preferably has 7 to 12 carbon atoms. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane and tetracyclododecane.

The aryl group for R⁹¹ preferably has 6 to 18 carbon atoms, and more preferably 6 to 10 carbon atoms. Specifically, a phenyl group is particularly desirable.

As the aralkyl group for R⁹¹, an aralkyl group in which an alkylene group having 1 to 8 carbon atoms has been bonded to the aforementioned “aryl group for R⁹¹” is preferable, an aralkyl group in which an alkylene group of 1 to 6 carbon atoms has been bonded to the aforementioned “aryl group for R⁹¹” is more preferable, and an aralkyl group in which an alkylene group having 1 to 4 carbon atoms has been bonded to the aforementioned “aryl group for R⁹¹” is most preferable.

The hydrocarbon group for R⁹¹ preferably has part or all of the hydrogen atoms within the hydrocarbon group substituted with fluorine, and the hydrocarbon group more preferably has 30 to 100% of the hydrogen atoms substituted with fluorine. Among these, a perfluoroalkyl group in which all of the hydrogen atoms within the alkyl group have been substituted with fluorine atoms is particularly desirable.

The hydrocarbon group for R⁹¹ may have a substituent. Examples of the substituent include a halogen atom, an oxo group (═O), a hydroxy group (—OH), an amino group (—NH₂) and —SO₂—NH₂. Further, part of the carbon atoms constituting the hydrocarbon group may be substituted with a substituent containing a hetero atom. Examples of the substituent containing a hetero atom include —O—, —NH—, —N═, —C(═O)—O—, —S—, —S(═O)₂— and —S(═O)₂—O—.

As the hydrocarbon group for R⁹¹, examples of the hydrocarbon group having a substituent include lactone-containing cyclic groups represented by the aforementioned general formulae (a2-r-1) to (a2-r-7).

Further, as R⁹¹, examples of the hydrocarbon group having a substituent include —SO₂— containing cyclic groups represented by general formulae (a5-r-1) to (a5-r-4); and substituted aryl groups and monocyclic heterocyclic groups represented by chemical formulae shown below.

As the structural unit (a9), a structural unit represented by general formula (a9-1-1) shown below is preferable.

In the formula, R is the same as defined above; Ya⁹¹ represents a single bond or a divalent linking group; R⁹¹ represents a hydrocarbon group optionally having a substituent; and Ya⁹² represents an oxygen atom or a sulfur atom.

In general formula (a9-1-1), Ya⁹¹, R⁹¹ and R are the same as defined above.

R⁹² represents an oxygen atom or a sulfur atom.

Specific examples of structural units represented by general formula (a9-1) or (a9-1-1) are shown below. In the following formulae, R^(α) represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a9) contained in the component (A1), 1 kind of structural unit may be used, or 2 or more kinds may be used.

When the component (A1) contains the structural unit (a9), the amount of the structural unit (a9) based on the combined total (100 mol %) of all structural units constituting the component (A1) is preferably 1 to 40 mol %, more preferably 3 to 30 mol %, still more preferably 5 to 25 mol %, and most preferably 10 to 20 mol %.

When the amount of the structural unit (a9) is at least as large as the lower limit of the above-mentioned range, for example, the acid diffusion length may be appropriately adjusted, the adhesion of the resist film to a substrate may be enhanced, the solubility during development may be appropriately adjusted, and the etching resistance may be improved. On the other hand, when the amount of the structural unit (a9) is no more than the upper limit of the above-mentioned range, a good balance may be achieved with the other structural units, and the lithography properties may be improved.

In the resist composition, as the component (A1), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

In the resist composition of the present embodiment, the component (A1) is a polymeric compound having the structural unit (a0), and preferable examples thereof include a copolymer having any other desired structural unit.

Preferable examples of the component (A1) include a polymeric compound having a repeating structure of the structural unit (a0) and the structural unit (a10); a polymeric compound having a repeating structure of the structural unit (a0), the structural unit (a1) and the structural unit (a2); and a polymeric compound having a repeating structure of the structural unit (a0), the structural unit (a2) and the structural unit (a3).

The component (A1) may be produced, for example, by dissolving the monomers corresponding with each of the structural units in a polymerization solvent, followed by addition of a radical polymerization initiator such as azobisisobutyronitrile (AIBN) or dimethyl-2,2′-azobisisoutyrate (e.g., V-601). Alternatively, the component (A1) may be prepared by dissolving a monomer from which the structural unit (a0) is derived, and a precursor monomer (monomer for which the functional group is protected) from which the structural unit other than the structural unit (a0) is derived in a polymerization solvent, polymerizing the dissolved monomers using the radical polymerization initiator described above, followed by performing a deprotection reaction. In the polymerization, a chain transfer agent such as HS—CH₂—CH₂—CH₂—C(CF₃)₂—OH may be used to introduce a —C(CF₃)₂—OH group at the terminal(s) of the polymer. Such a copolymer having introduced a hydroxyalkyl group in which some of the hydrogen atoms of the alkyl group are substituted with fluorine atoms is effective in reducing developing defects and LER (line edge roughness: unevenness of the side walls of a line pattern).

The weight average molecular weight (Mw) (the polystyrene equivalent value determined by gel permeation chromatography (GPC)) of the component (A1) is not particularly limited, but is preferably 1,000 to 50,000, more preferably 2,000 to 30,000, and still more preferably 3,000 to 20,000.

When the Mw of the component (A1) is no more than the upper limit of the above-mentioned preferable range, the resist composition exhibits a satisfactory solubility in a resist solvent. On the other hand, when the Mw of the component (A1) is at least as large as the lower limit of the above-mentioned preferable range, dry etching resistance and the cross-sectional shape of the resist pattern becomes satisfactory.

The dispersity (Mw/Mn) of the component (A1) is not particularly limited, but is preferably 1.0 to 4.0, more preferably 1.0 to 3.0, and most preferably 1.1 to 2.0. Here, Mn is the number average molecular weight.

Base Component Other than (A1)

In the resist composition of the present embodiment, as the component (A), “a base component which exhibits changed solubility in a developing solution under action of acid” other than the component (A1) may be used in combination. Such base component other than the component (A1) is not particularly limited, and any of the multitude of conventional base components used within chemically amplified resist compositions may be appropriately selected for use. As such base component other than the component (A1), one kind of a polymer or a low molecular weight compound may be used, or a combination of two or more kinds may be used.

In the resist composition of the present embodiment, the amount of the component (A) may be appropriately adjusted depending on the thickness of the resist film to be formed, and the like.

<Compound (D0)>

In the resist composition of the present embodiment, the component (D0) is a compound represented by general formula (d0) shown below. The component (D0) is a compound composed of a cation moiety and an anion moiety.

In formula (d0), Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group; Rd⁰² represents a substituent; q represents an integer of 0 to 3; n1 represents an integer of 1 or more; n2 represents an integer of 0 or more; provided that n1+n2≤(q×2)+5; m represents an integer of 1 or more; and M^(m+) represents an m-valent organic cation.

Anion Moiety

In formula (d0), Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group. Examples of the fluorinated alkyl group for Rd⁰¹ groups in which part or all of the hydrogen atoms within the alkyl group of 1 to 5 carbon atoms have been substituted with a fluorine atom. Further, the alkyl group is preferably a linear alkyl group or a branched alkyl group. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group. Among these, a methyl group or ethyl group is preferable, and a methyl group is particularly desirable.

Among these examples, as Rd⁰¹, a fluorine atom or a trifluoromethyl group is preferable.

In formula (d0), Rd⁰² represents a substituent. Examples of the substituent include a hydrocarbon group, an alkoxy group, an acyl group, a hydroxy group and a hydroxyalkyl group.

Examples of the hydrocarbon group as the substituent include a linear or branched alkyl group, an aliphatic cyclic hydrocarbon group, and an aromatic hydrocarbon group.

As the linear or branched alkyl group, a linear or branched alkyl group of 1 to 5 carbon atoms is preferable, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an n-butyl group, a tert-butyl group and a pentyl group.

As the aliphatic cyclic hydrocarbon group, an aliphatic cyclic hydrocarbon group having 3 to 6 carbon atoms is preferable, and specific examples thereof include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, and a cyclohexyl group.

As the aromatic hydrocarbon group, an aromatic hydrocarbon group having 6 to 30 carbon atoms is preferable, and specific examples thereof include a group in which 1 hydrogen atom has been removed from an aromatic hydrocarbon ring such as benzene, biphenyl, fluorene, naphthalene, anthracene or phenanthrene. Among these examples, a group in which 1 hydrogen atom has been removed from benzene (phenyl group) is preferable.

The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, and specific examples thereof include a methoxy group, an ethoxy group, a propoxy group, an n-butoxy group, a tert-butoxy group, and a pentyloxy group. Among these examples, a methoxy group is preferable.

The acyl group as the substituent is preferably an acyl group having 1 to 3 carbon atoms, and specific examples thereof include a formyl group, an acetyl group, and a propionyl group.

The hydroxyalkyl group as the substituent is preferably a hydroxyalkyl group having 1 to 5 carbon atoms, and specific examples thereof include a hydroxymethyl group, a hydroxyethyl group, a hydroxypropyl group, a hydroxybutyl group, and a hydroxypentyl group.

Among these examples, in terms of acid diffusion control, Rd⁰² is preferably a hydroxy group.

In formula (d0), n1 represents an integer of 1 or more, and n2 represents an integer of 0 or more. When n1 is an integer of 2 or more, the plurality of the substituents Rd⁰¹ (fluorine atom or fluorinated alkyl group) may be the same or different from each other. Further, when n2 is an integer of 2 or more, the plurality of the substituents Rd⁰² may be the same or different from each other.

In formula (d0), q represents an integer of 0 to 3. That is, the anion moiety of formula (d0), when q is 0, becomes a benzene structure; when q is 1, becomes a naphthalene structure; when q is 2, becomes an anthracene structure; and when q is 3, becomes a tetracene structure.

Further, n1+n2≤(q×2)+5. That is, in the benzene structure, the naphthalene structure, the anthracene structure or the tetracene structure, all hydrogen atoms other than the hydrogen atom substituted with a carboxylate group may be substituted with the aforementioned substituents, a fluorine atom or a fluorinated alkyl group. However, the anion moiety of formula (d0) has at least one fluorine atom or fluorinated alkyl group.

Specific examples of preferable anion moieties for the component (D0) are shown below.

Among the above examples, as the anion moiety of the component (D0), an anion represented by any one of the chemical formulae (an-d0-1) to (an-d0-5) is preferable.

Cation Moiety ((M^(m+))_(1/m))

In formula (d0), M^(m+) represents an m-valent organic cation. m represents an integer of 1 or more.

Among the organic cations, a sulfonium cation or an iodonium cation is preferable, and examples thereof include organic cations represented by general formulae (ca-1) to (ca-4) shown below.

In the formula, R²⁰¹ to R²⁰⁷, R²¹¹ and R²¹² each independently represents an aryl group which may have a substituent, an alkyl group which may have a substituent or an alkenyl group which may have a substituent. R²⁰¹ to R²⁰³, R²⁰⁶ and R²⁰⁷, and R²¹¹ and R²¹² may be mutually bonded to form a ring with the sulfur atom. R²⁰⁸ and R²⁰⁹ each independently represents a hydrogen atom or an alkyl group of 1 to 5 carbon atoms, or R²⁰⁸ and R²⁰⁹ may be mutually bonded to form a ring with the sulfur atom. R²¹⁰ represents an aryl group which may have a substituent, an alkyl group which may have a substituent, an alkenyl group which may have a substituent, or an —SO₂— containing cyclic group which may have a substituent. L²⁰¹ represents —C(═O)— or —C(═O)—O—. Each of the plurality of Y²⁰¹ independently represents an arylene group, an alkylene group or an alkenylene group. x represents 1 or 2. W²⁰¹ represents an (x+1) valent linking group.

As the aryl group for R²⁰¹ to R²⁰⁷ and R²¹¹ to R²¹², an aryl group of 6 to 20 carbon atoms may be mentioned, and a phenyl group or a naphthyl group is preferable.

The alkyl group for R²⁰¹ to R²⁰⁷, R²¹¹ and R²¹² is preferably a chain-like or cyclic alkyl group having 1 to 30 carbon atoms.

The alkenyl group for R²⁰¹ to R²⁰⁷ and R²¹¹ to R²¹² preferably has 2 to 10 carbon atoms.

Specific examples of the substituent which R²⁰¹ to R²⁰⁷ and R²¹¹ to R²¹² may have include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, and groups represented by general formulae (ca-r-1) to (ca-r-7) shown below.

In the formulae, each R′²⁰¹ independently represents a hydrogen atom, a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent, or a chain-like alkenyl group which may have a substituent.

As the cyclic group which may have a substituent, the chain-like alkyl group which may have a substituent and the chain-like alkenyl group which may have a substituent for R′²⁰¹, the same groups as those described later for R¹⁰¹ in formula (b-1) can be mentioned. As the cyclic group which may have a substituent and chain-like alkyl group which may have a substituent, the same groups as those described above for the acid dissociable group represented by the aforementioned formula (a1-r-2) can be also mentioned.

When R²⁰¹ to R²⁰³, R²⁰⁶, R²⁰⁷, R²¹¹ and R²¹² are mutually bonded to form a ring with the sulfur atom, these groups may be mutually bonded via a hetero atom such as a sulfur atom, an oxygen atom or a nitrogen atom, or a functional group such as a carbonyl group, —SO—, —SO₂—, —SO₃—, —COO—, —CONH— or —N(R_(N))— (wherein R_(N) represents an alkyl group of 1 to 5 carbon atoms). The ring containing the sulfur atom in the skeleton thereof is preferably a 3 to 10-membered ring, and most preferably a 5 to 7-membered ring. Specific examples of the ring formed include a thiophene ring, a thiazole ring, a benzothiophene ring, a thianthrene ring, a benzothiophene ring, a dibenzothiophene ring, a 9H-thioxanthene ring, a thioxanthone ring, a phenoxathiin ring, a tetrahydrothiophenium ring, and a tetrahydrothiopyranium ring.

R²⁰⁸ and R²⁰⁹ each independently represents a hydrogen atom or an alkyl group of 1 to 5 carbon atoms, preferably a hydrogen atom or an alkyl group of 1 to 3 carbon atoms, and when R²⁰⁸ and R²⁰⁹ each represents an alkyl group, R²⁰⁸ and R²⁰⁹ may be mutually bonded to form a ring.

R²¹⁰ represents an aryl group which may have a substituent, an alkyl group which may have a substituent, an alkenyl group which may have a substituent, or an —SO₂— containing cyclic group which may have a substituent.

Examples of the aryl group for R²¹⁰ include an unsubstituted aryl group of 6 to 20 carbon atoms, and a phenyl group or a naphthyl group is preferable.

As the alkyl group for R²¹⁰, a chain-like or cyclic alkyl group having 1 to 30 carbon atoms is preferable.

The alkenyl group for R²¹⁰ preferably has 2 to 10 carbon atoms.

As the —SO₂— containing cyclic group for R²¹⁰ which may have a substituent, an “—SO₂— containing polycyclic group” is preferable, and a group represented by the aforementioned general formula (a5-r-1) is more preferable.

Each Y²⁰¹ independently represents an arylene group, an alkylene group or an alkenylene group.

Examples of the arylene group for Y²⁰¹ include groups in which one hydrogen atom has been removed from an aryl group given as an example of the aromatic hydrocarbon group for R¹⁰¹ in formula (b-1) described later.

Examples of the alkylene group and alkenylene group for Y²⁰¹ include groups in which one hydrogen atom has been removed from the chain-like alkyl group or the chain-like alkenyl group given as an example of R¹⁰¹ in formula (b-1) described later.

In the formula (ca-4), x represents 1 or 2.

W²⁰¹ represents a linking group having a valency of (x+1), i.e., a divalent or trivalent linking group.

As the divalent linking group for W²⁰¹, a divalent hydrocarbon group which may have a substituent is preferable, and as examples thereof, the same hydrocarbon groups (which may have a substituent) as those described above for Ya²¹ in the general formula (a2-1) can be mentioned. The divalent linking group for W²⁰¹ may be linear, branched or cyclic, and cyclic is more preferable. Among these, an arylene group having two carbonyl groups, each bonded to the terminal thereof is preferable. Examples of the arylene group include a phenylene group and a naphthylene group, and a phenylene group is particularly desirable.

As the trivalent linking group for W²⁰¹, a group in which one hydrogen atom has been removed from the aforementioned divalent linking group for W²⁰¹ and a group in which the divalent linking group has been bonded to another divalent linking group can be mentioned. The trivalent linking group for W²⁰¹ is preferably a group in which 2 carbonyl groups are bonded to an arylene group.

Specific examples of preferable cations represented by formula (ca-1) include cations represented by formulae (ca-1-1) to (ca-1-78) and (ca-1-101) to (ca-1-149) shown below.

In the following chemical formulae, g1 represents a repeating number, and g1 is an integer of 1 to 5. g2 represents a repeating number, and g2 is an integer of 0 to 20. g3 represents a repeating number, and g3 is an integer of 0 to 20.

In the formulae, R″²⁰¹ represents a hydrogen atom or a substituent. Examples of the substituent which R²⁰¹ to R²⁰⁷, R²¹¹ and R²¹² may have include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, and groups respectively represented by formulae (ca-r-1) to (ca-r-7).

Specific examples of suitable cations represented by formula (ca-2) include cations respectively represented by the following formulae (ca-2-1) to (ca-2-2), a dihphenyliodonium cation and a bis(4-tert-butylphenyl)iodonium cation.

Specific examples of suitable cations represented by formula (ca-3) include cations respectively represented by formulae (ca-3-1) to (ca-3-7) shown below.

Specific examples of preferable cations represented by formula (ca-4) include cations represented by formulae (ca-4-1) and (ca-4-2) shown below.

Among these examples, as the cation moiety ((M^(m+))_(1/m)), a cation represented by general formula (ca-1) is preferable. Specifically, cations represented by chemical formulae (ca-1-1) to (ca-1-78) and (ca-1-101) to (ca-1-149) are preferable, and a cation represented by chemical formula (ca-1-101) is more preferable.

In the resist composition of the present embodiment, the component (D0) is preferably a compound represented by general formula (d0-1) shown below having an anion moiety and a cation moiety.

In formula (d0-1), R^(d11) represents an aryl group which may have a substituent; R^(d12) and R^(d13) each independently represents an aryl group which may have a substituent, or R^(d12) and R^(d13) are mutually bonded to form a ring with the sulfur atom; Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group; Rd⁰² represents a substituent; q represents an integer of 0 to 3; n1 represents an integer of 1 or more; n2 represents an integer of 0 or more; provided that n1+n2≤(q×2)+5.

In formula (d0-1), the anion moiety is the same as defined for the anion moiety of the aforementioned formula (d0). In formula (d0-1), R^(d11) to R^(d13) are the same as defined for the aryl group (which may have a substituent) for R²⁰¹ to R²⁰³ in the aforementioned formula (ca-1). The cyclic structure formed by R^(d12) and R^(d13) being mutually bonded together with the sulfur atom is the same as defined for the cyclic structure formed by R²⁰¹ to R²⁰³ being mutually bonded together with the sulfur atom in the aforementioned formula (ca-1).

Specifically, as the component (D0), a combination of a cation moiety represented by any one of chemical formulae (ca-1-1) to (ca-1-78) and (ca-1-101) to (ca-1-149) with an anion moiety represented by any one of chemical formulae (an-d0-1) to (an-d0-9) is preferable. Among these examples, a combination of a cation moiety represented by chemical formula (ca-1-101) with an anion moiety represented by any one of chemical formulae (an-d0-1) to (an-d0-5) is more preferable.

Specific examples of the component (D0) are shown below, although the component (D0) is not limited to these examples.

In the resist composition of the present embodiment, as the component (D0), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

In the resist composition of the present embodiment, the amount of the component (D0) relative to 100 parts by weight of the component (A) is preferably 1 to 35 parts by weight, more preferably from 2 to 30 parts by weight, still more preferably from 3 to 25 parts by weight, and most preferably 3 to 20 parts by weight.

When the amount of the component (D0) is at least as large as the lower limit of the above-mentioned preferable range, satisfactory lithography properties (reduced roughness, improved resolution, and the like) and a good resist pattern shape may be more reliably obtained. On the other hand, when the amount of the component (D0) is no more than the upper limit of the above-mentioned preferable range, a good balance may be achieved with the other components, and the lithography properties may be improved.

<Optional Components>

The resist composition of the present embodiment may contain, in addition to the aforementioned components (A) and (D0), any other optional components.

Examples of the optional components include the component (B), the component (D) (provided that the component (D0) is excluded), the component (E), the component (F) and the component (S) described below.

<<Component (B)>>

The component (B) is an acid generator component which generates acid upon exposure.

As the component (B), there is no particular limitation, and any of the known acid generators used in conventional chemically amplified resist compositions may be used.

Examples of these acid generators are numerous, and include onium salt acid generators such as iodonium salts and sulfonium salts; oxime sulfonate acid generators; diazomethane acid generators such as bisalkyl or bisaryl sulfonyl diazomethanes and poly(bis-sulfonyl)diazomethanes; nitrobenzylsulfonate acid generators; iminosulfonate acid generators; and disulfone acid generators.

As the onium salt acid generator, a compound represented by general formula (b-1) below (hereafter, sometimes referred to as “component (b-1)”), a compound represented by general formula (b-2) below (hereafter, sometimes referred to as “component (b-2)”) or a compound represented by general formula (b-3) below (hereafter, sometimes referred to as “component (b-3)”) may be mentioned.

In the formulae, R¹⁰¹ and R¹⁰⁴ to R¹⁰⁸ each independently represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, provided that R¹⁰⁴ and R¹⁰⁵ may be mutually bonded to form a ring; R¹⁰² represents a fluorine atom or a fluorinated alkyl group of 1 to 5 carbon atoms; Y¹⁰¹ represents a single bond or a divalent linking group containing an oxygen atom; V¹⁰¹ to V¹⁰³ each independently represents a single bond, an alkylene group or a fluorinated alkylene group; L¹⁰¹ and L¹⁰² each independently represents a single bond or an oxygen atom; L¹⁰³ to L¹⁰⁵ each independently represents a single bond, —CO— or —SO₂—; and m represents an integer of 1 or more; and M′^(m+) represents an m-valent onium cation.

{Anion Moiety}

Anion Moiety of Component (b-1)

In the formula (b-1), R¹⁰¹ represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent.

Cyclic Group which May have a Substituent:

The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be either an aromatic hydrocarbon group or an aliphatic hydrocarbon group. An “aliphatic hydrocarbon group” refers to a hydrocarbon group that has no aromaticity. The aliphatic hydrocarbon group may be either saturated or unsaturated, but in general, the aliphatic hydrocarbon group is preferably saturated.

The aromatic hydrocarbon group for R¹⁰¹ is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon ring preferably has 3 to 30 carbon atoms, more preferably 5 to 30, still more preferably 5 to 20, still more preferably 6 to 15, and most preferably 6 to 10. Here, the number of carbon atoms within a substituent(s) is not included in the number of carbon atoms of the aromatic hydrocarbon group.

Examples of the aromatic ring contained in the aromatic hydrocarbon group represented by R¹⁰¹ include benzene, fluorene, naphthalene, anthracene, phenanthrene and biphenyl; and aromatic hetero rings in which part of the carbon atoms constituting the aforementioned aromatic rings has been substituted with a hetero atom. Examples of the hetero atom within the aromatic hetero rings include an oxygen atom, a sulfur atom and a nitrogen atom.

Specific examples of the aromatic hydrocarbon group represented by R¹⁰¹ include a group in which one hydrogen atom has been removed from the aforementioned aromatic ring (i.e., an aryl group, such as a phenyl group or a naphthyl group), and a group in which one hydrogen of the aforementioned aromatic ring has been substituted with an alkylene group (e.g., an arylalkyl group such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group or a 2-naphthylethyl group). The alkylene group (alkyl chain within the arylalkyl group) preferably has 1 to 4 carbon atom, more preferably 1 or 2, and most preferably 1.

Examples of the cyclic aliphatic hydrocarbon group for R¹⁰¹ include aliphatic hydrocarbon groups containing a ring in the structure thereof.

As examples of the hydrocarbon group containing a ring in the structure thereof, an alicyclic hydrocarbon group (a group in which one hydrogen atom has been removed from an aliphatic hydrocarbon ring), a group in which the alicyclic hydrocarbon group is bonded to the terminal of the aforementioned chain-like aliphatic hydrocarbon group, and a group in which the alicyclic group is interposed within the aforementioned linear or branched aliphatic hydrocarbon group, can be given.

The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.

The alicyclic hydrocarbon group may be either a polycyclic group or a monocyclic group. As the monocyclic alicyclic hydrocarbon group, a group in which one or more hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. As the polycyclic alicyclic hydrocarbon group, a group in which one or more hydrogen atoms have been removed from a polycycloalkane is preferable, and the polycyclic group preferably has 7 to 30 carbon atoms. Among polycycloalkanes, a polycycloalkane having a bridged ring polycyclic skeleton, such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclodpdecane, and a polycycloalkane having a condensed ring polycyclic skeleton, such as a cyclic group having a steroid skeleton are preferable.

Among these examples, as the cyclic aliphatic hydrocarbon group for R¹⁰¹, a group in which one or more hydrogen atoms have been removed from a monocycloalkane or a polycycloalkane is preferable, a group in which one or more hydrogen atoms have been removed from a polycycloalkane is more preferable, an adamantyl group or a norbornyl group is still more preferable, and an adamantyl group is most preferable.

The linear or branched aliphatic hydrocarbon group which may be bonded to the alicyclic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, still more preferably 1 to 4 carbon atoms, and most preferably 1 to 3 carbon atoms.

As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specific examples thereof include a methylene group [—CH₂—], an ethylene group [—(CH₂)₂—], a trimethylene group [—(CH₂)₃—], a tetramethylene group [—(CH₂)₄-] and a pentamethylene group [—(CH₂)₅—].

As the branched aliphatic hydrocarbon group, branched alkylene groups are preferred, and specific examples include various alkylalkylene groups, including alkylmethylene groups such as —CH(CH₃)—, —CH(CH₂CH₃)—, —C(CH₃)₂—, —C(CH₃)(CH₂CH₃)—, —C(CH₃)(CH₂CH₂CH₃)—, and —C(CH₂CH₃)₂—; alkylethylene groups such as —CH(CH₃)CH₂—, —CH(CH₃)CH(CH₃)—, —C(CH₃)₂CH₂—, —CH(CH₂CH₃)CH₂—, and —C(CH₂CH₃)₂—CH₂—; alkyltrimethylene groups such as —CH(CH₃)CH₂CH₂—, and —CH₂CH(CH₃)CH₂—; and alkyltetramethylene groups such as —CH(CH₃)CH₂CH₂CH₂—, and —CH₂CH(CH₃)CH₂CH₂—. As the alkyl group within the alkylalkylene group, a linear alkyl group of 1 to 5 carbon atoms is preferable.

The cyclic hydrocarbon group for R¹⁰¹ may contain a hetero atom such as a heterocycle. Specific examples include lactone-containing cyclic groups represented by the aforementioned general formulae (a2-r-1) to (a2-r-7), the —SO₂— containing cyclic group represented by the aforementioned formulae (a5-r-1) to (a5-r-4), and other heterocyclic groups represented by the aforementioned chemical formulae (r-hr-1) to (r-hr-16).

As the substituent for the cyclic group for R¹⁰¹, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group or the like may be used.

The alkyl group as the substituent is preferably an alkyl group of 1 to 12 carbon atoms, and a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group is particularly desirable.

The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group or tert-butoxy group, and most preferably a methoxy group or an ethoxy group.

Examples of the halogen atom for the substituent include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.

Example of the aforementioned halogenated alkyl group includes a group in which a part or all of the hydrogen atoms within an alkyl group of 1 to 5 carbon atoms (e.g., a methyl group, an ethyl group, a propyl group, an n-butyl group or a tert-butyl group) have been substituted with the aforementioned halogen atoms.

The carbonyl group as the substituent is a group that substitutes a methylene group (—CH₂—) constituting the cyclic hydrocarbon group.

Chain Alkyl Group which May have a Substituent:

The chain-like alkyl group for R¹⁰¹ may be linear or branched.

The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15, and most preferably 1 to 10. Specific examples include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, an undecyl group, a dodecyl group, a tridecyl group, an isotridecyl group, a tetradecyl group, a pentadecyl group, a hexadecyl group, an isohexadecyl group, a heptadecyl group, an octadecyl group, a nonadecyl group, an icosyl group, a henicosyl group and a docosyl group.

The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15, and most preferably 3 to 10. Specific examples include a 1-methylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group and a 4-methylpentyl group.

Chain Alkenyl Group which May have a Substituent:

The chain-like alkenyl group for R¹⁰¹ may be linear or branched, and preferably has 2 to 10 carbon atoms, more preferably 2 to 5 carbon atoms, still more preferably 2 to 4 carbon atoms, and most preferably 3 carbon atoms. Examples of linear alkenyl groups include a vinyl group, a propenyl group (an allyl group) and a butynyl group. Examples of branched alkenyl groups include a 1-methylvinyl group, a 2-methylvinyl group, a 1-methylpropenyl group and a 2-methylpropenyl group.

Among these examples, as the chain-like alkenyl group, a linear alkenyl group is preferable, a vinyl group or a propenyl group is more preferable, and a vinyl group is most preferable.

As the substituent for the chain-like alkyl group or alkenyl group for R¹⁰¹, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, a cyclic group for R¹⁰¹ or the like may be used.

Among the above examples, as R¹⁰¹, a cyclic group which may have a substituent is preferable, and a cyclic hydrocarbon group which may have a substituent is more preferable. As the substituent, a hydroxy group, a carbonyl group, a nitro group or an amino group is preferable. Among these examples, a hydroxy group is preferable in that the component (B) may be reliably distributed on a substrate side within the resist film.

Specific examples of the cyclic hydrocarbon group include a phenyl group, a naphthyl group, a group in which one hydrogen atom has been removed from a polycycloalkane, a lactone-containing cyclic group represented by any one of the aforementioned general formulae (a2-r-1) to (a2-r-7); and an —SO₂— containing cyclic group represented by any one of the aforementioned formula (a5-r-1) to (a5-r-4).

In formula (b-1), Y¹⁰¹ represents a single bond or a divalent linking group containing an oxygen atom.

In the case where Y¹⁰¹ is a divalent linking group containing an oxygen atom, Y¹⁰¹ may contain an atom other than an oxygen atom. Examples of atoms other than an oxygen atom include a carbon atom, a hydrogen atom, a sulfur atom and a nitrogen atom.

Examples of divalent linking groups containing an oxygen atom include non-hydrocarbon, oxygen atom-containing linking groups such as an oxygen atom (an ether bond; —O—), an ester bond (—C(═O)—O—), an oxycarbonyl group (—O—C(═O)—), an amido bond (—C(═O)—NH—), a carbonyl group (—C(═O)—) and a carbonate bond (—O—C(═O)—O—); and combinations of the aforementioned non-hydrocarbon, hetero atom-containing linking groups with an alkylene group. Furthermore, the combinations may have a sulfonyl group (—SO₂—) bonded thereto. Examples of divalent linking groups containing an oxygen atom include linking groups represented by general formulae (y-al-1) to (y-al-7) shown below.

In the formulae, V′¹⁰¹ represents a single bond or an alkylene group of 1 to 5 carbon atoms; V′¹⁰² represents a divalent saturated hydrocarbon group of 1 to 30 carbon atoms.

The divalent saturated hydrocarbon group for V′¹⁰² is preferably an alkylene group of 1 to 30 carbon atoms, more preferably an alkylene group of 1 to 10 carbon atoms, and still more preferably an alkylene group of 1 to 5 carbon atoms.

The alkylene group for V′¹⁰¹ and V′¹⁰² may be a linear alkylene group or a branched alkylene group, and a linear alkylene group is preferable.

Specific examples of the alkylene group for V′¹⁰¹ and V′¹⁰² include a methylene group [—CH₂—]; an alkylmethylene group, such as —CH(CH₃)—, —CH(CH₂CH₃)—, —C(CH₃)₂—, —C(CH₃)(CH₂CH₃)—, —C(CH₃)(CH₂CH₂CH₃)— and —C(CH₂CH₃)₂—; an ethylene group [—CH₂CH₂—]; an alkylethylene group, such as —CH(CH₃)CH₂—, —CH(CH₃)CH(CH₃)—, —C(CH₃)₂CH₂— and —CH(CH₂CH₃)CH₂—; a trimethylene group (n-propylene group) [—CH₂CH₂CH₂—]; an alkyltrimethylene group, such as —CH(CH₃)CH₂CH₂— and —CH₂CH(CH₃)CH₂—; a tetramethylene group [—CH₂CH₂CH₂CH₂—]; an alkyltetramethylene group, such as —CH(CH₃)CH₂CH₂CH₂—, —CH₂CH(CH₃)CH₂CH₂—; and a pentamethylene group [—CH₂CH₂CH₂CH₂CH₂—].

Further, part of methylene group within the alkylene group for V′¹⁰¹ and V′¹⁰² may be substituted with a divalent aliphatic cyclic group of 5 to 10 carbon atoms. The aliphatic cyclic group is preferably a divalent group in which one hydrogen atom has been removed from the cyclic aliphatic hydrocarbon group (monocyclic aliphatic hydrocarbon group or polycyclic aliphatic hydrocarbon group) for Ra′³ in the aforementioned formula (a1-r-1), and a cyclohexylene group, 1,5-adamantylene group or 2,6-adamantylene group is preferable.

Y¹⁰¹ is preferably a divalent linking group containing an ether bond or a divalent linking group containing an ester bond, and groups represented by the aforementioned formulas (y-al-1) to (y-al-5) are preferable.

In formula (b-1), V¹⁰¹ represents a single bond, an alkylene group or a fluorinated alkylene group. The alkylene group and the fluorinated alkylene group for V¹⁰¹ preferably has 1 to 4 carbon atoms. Examples of the fluorinated alkylene group for V¹⁰¹ include a group in which part or all of the hydrogen atoms within the alkylene group for V¹⁰¹ have been substituted with fluorine. Among these examples, as V¹⁰¹, a single bond or a fluorinated alkylene group of 1 to 4 carbon atoms is preferable.

In formula (b-1), R¹⁰² represents a fluorine atom or a fluorinated alkyl group of 1 to 5 carbon atoms. R¹⁰² is preferably a fluorine atom or a perfluoroalkyl group of 1 to 5 carbon atoms, and more preferably a fluorine atom.

As a specific example of the anion moiety for the component (b-1), in the case where Y¹⁰¹ a single bond, a fluorinated alkylsulfonate anion such as a trifluoromethanesulfonate anion or a perfluorobutanesulfonate anion can be mentioned; and in the case where Y¹⁰¹ represents a divalent linking group containing an oxygen atom, anions represented by formulae (an-1) to (an-3) shown below can be mentioned.

In the formulae, R″¹⁰¹ represents an aliphatic cyclic group which may have a substituent, a group represented by any one of the aforementioned formulae (r-hr-1) to (r-hr-6), or a chain alkyl group which may have a substituent; R″¹⁰² represents an aliphatic cyclic group which may have a substituent, a lactone-containing cyclic group represented by any of the aforementioned formulae (a2-r-1) to (a2-r-7), or an —SO₂— containing cyclic group represented by any of formulae (a5-r-1) to (a5-r-4); R″¹⁰³ represents an aromatic cyclic group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain alkenyl group which may have a substituent; V″¹⁰¹ represents a single bond, an alkylene group having 1 to 4 carbon atoms or a fluorinated alkylene group having 1 to 4 carbon atoms; R¹⁰² represents a fluorine atom or a fluorinated alkyl group of 1 to 5 carbon atoms; each v″ independently represents an integer of 0 to 3; each q″ independently represents an integer of 1 to 20; and n″ represents 0 or 1.

As the aliphatic cyclic group for R″¹⁰¹, R″¹⁰² and R″¹⁰³ which may have a substituent, the same groups as the cyclic aliphatic hydrocarbon group for R¹⁰¹ described above are preferable.

As the substituent, the same groups as those described above for substituting the cyclic aliphatic hydrocarbon group for R¹⁰¹ may be mentioned. Among these examples, a hydroxy group, a carbonyl group, a nitro group or an amino group is preferable. Among these examples, a hydroxy group is preferable in that the component (B) may be reliably distributed on a substrate side within the resist film.

As the aromatic cyclic group for R″¹⁰³ which may have a substituent, the same groups as the aromatic hydrocarbon group for the cyclic hydrocarbon group represented by R^(° 0) described above are preferable. The substituent is the same as defined for the substituent for the aromatic hydrocarbon group represented by R¹⁰¹.

As the chain-like alkyl group for R″¹⁰¹ which may have a substituent, the same groups as those described above for R¹⁰¹ are preferable. As the chain-like alkenyl group for R″¹⁰³ which may have a substituent, the same groups as those described above for R¹⁰¹ are preferable.

In the formulae (an-1) to (an-3), V″¹⁰¹ represents a single bond, an alkylene group having 1 to 4 carbon atoms or a fluorinated alkylene group having 1 to 4 carbon atoms. V″¹⁰¹ is preferably a single bond, an alkylene group having 1 carbon atom (methylene group), or a fluorinated alkylene group having 1 to 3 carbon atoms.

In formulae (an-1) to (an-3), R¹⁰² represents a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. R¹⁰² is preferably a perfluoroalkyl group having 1 to 5 carbon atoms or a fluorine atom, and more preferably a fluorine atom.

In formulae (an-1) to (an-3), v″ represents an integer of 0 to 3, and is preferably 0 or 1. q″ represents an integer of 1 to 20, preferably an integer of 1 to 10, more preferably an integer of 1 to 5, still more preferably 1, 2 or 3, and most preferably 1 or 2. n″ represents 0 or 1.

Anion Moiety of Component (b-2)

In formula (b-2), R¹⁰⁴ and R¹⁰⁵ each independently represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same as defined for R¹⁰¹ in formula (b-1). R¹⁰⁴ and R¹⁰⁵ may be mutually bonded to form a ring. As R¹⁰⁴ and R¹⁰⁵, a chain-like alkyl group which may have a substituent is preferable, and a linear or branched alkyl group or a linear or branched fluorinated alkyl group is more preferable.

The chain-like alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms, and still more preferably 1 to 3 carbon atoms. The smaller the number of carbon atoms of the chain-like alkyl group for R¹⁰⁴ and R¹⁰⁵, the more the solubility in a resist solvent is improved. Further, in the chain-like alkyl group for R¹⁰⁴ and R¹⁰⁵, it is preferable that the number of hydrogen atoms substituted with fluorine atoms is as large as possible because the acid strength increases and the transparency to high energy radiation of 200 nm or less or electron beam is improved.

The fluorination ratio of the chain-like alkyl group is preferably from 70 to 100%, more preferably from 90 to 100%, and it is particularly desirable that the chain-like alkyl group be a perfluoroalkyl group in which all hydrogen atoms are substituted with fluorine atoms.

In formula (b-2), V¹⁰² and V¹⁰³ each independently represents a single bond, an alkylene group or a fluorinated alkylene group, and is the same as defined for V¹⁰¹ in formula (b-1).

In formula (b-2), L¹⁰¹ and L¹⁰² each independently represents a single bond or an oxygen atom.

Anion Moiety of Component (b-3)

In formula (b-3), R¹⁰⁶ to R¹⁰⁸ each independently represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same as defined for R¹⁰¹ in formula (b-1).

L¹⁰³ to L¹⁰⁵ each independently represents a single bond, —CO— or —SO₂—.

{Cation Moiety}

In formulae (b-1), (b-2), and (b-3), m represents an integer of 1 or greater, M′^(m+) represents an m-valent onium cation. As the onium cation moiety for M′^(m+), cations represented by the aforementioned general formulae (ca-1) to (ca-4) may be mentioned as preferable examples.

Among these examples, a cation represented by general formula (ca-1) is preferable, and specific examples thereof include cations represented by the aforementioned chemical formulae (ca-1-1) to (ca-1-78) and (ca-1-101) to (ca-1-149).

In the present embodiment, as the onium salt acid generator, among the components (b-1), (b-2) and (b-3), the component (b-1) is preferable.

In the resist composition of the present embodiment, as the component (B), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

When the resist composition contains the component (B), the amount of the component (B) relative to 100 parts by weight of the component (A) is preferably 50 parts by weight or less, more preferably 1 to 40 parts by weight, and still more preferably 5 to 30 parts by weight.

When the amount of the component (B) is within the above-mentioned range, formation of a resist pattern can be satisfactorily performed.

<<Component (D)>>

The resist composition according to the present embodiment may include, in addition to the component (A) and the component (D0), or in addition to the component (A), the component (D0) and the component (B), a basic component which does not fall under the definition of the component (D0) (component (D)). The component (D) functions as an acid diffusion control agent, i.e., a quencher which traps the acid generated in the resist composition upon exposure.

Examples of the component (D) include a nitrogen-containing organic compound (D1) (hereafter, referred to as “component (D1)”), and a photodegradable base (D2) (hereafter, referred to as “component (D2)”) which is decomposable by exposure to lose the ability of controlling of acid diffusion, and does not fall under the definition of the component (D1) and the component (D0).

When a resist pattern is formed using a resist composition containing the component (D), the contrast between exposed portions and unexposed portions of the resist film is further improved.

Component (D1)

The component (D1) is a basic component and is a nitrogen-containing organic compound component that acts as an acid diffusion control agent in the resist composition.

The component (D1) is not particularly limited as long as it acts as an acid diffusion control agent, and examples thereof include aliphatic amines and aromatic amines.

Among the aliphatic amines, secondary aliphatic amines and tertiary aliphatic amines are preferable.

An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 12 carbon atoms.

Examples of these aliphatic amines include amines in which at least one hydrogen atom of ammonia (NH₃) has been substituted with an alkyl group or hydroxyalkyl group of no more than 12 carbon atoms (i.e., alkylamines or alkylalcoholamines), and cyclic amines.

Specific examples of alkylamines and alkylalcoholamines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, and n-decylamine; dialkylamines such as diethylamine, di-n-propylamine, di-n-heptylamine, di-n-octylamine, and dicyclohexylamine; trialkylamines such as trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-hexylamine, tri-n-pentylamine, tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, and tri-n-dodecylamine; and alkyl alcohol amines such as diethanolamine, triethanolamine, diisopropanolamine, triisopropanolamine, di-n-octanolamine, and tri-n-octanolamine. Among these, trialkylamines of 5 to 10 carbon atoms are preferable, and tri-n-pentylamine and tri-n-octylamine are particularly desirable.

Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be a monocyclic compound (aliphatic monocyclic amine), or a polycyclic compound (aliphatic polycyclic amine).

Specific examples of the aliphatic monocyclic amine include piperidine, and piperazine.

The aliphatic polycyclic amine preferably has 6 to 10 carbon atoms, and specific examples thereof include 1,5-diazabicyclo[4.3.0]-5-nonene, 1,8-diazabicyclo[5.4.0]-7-undecene, hexamethylenetetramine, and 1,4-diazabicyclo[2.2.2]octane.

Examples of other aliphatic amines include tris(2-methoxymethoxyethyl)amine, tris {2-(2-methoxyethoxy)ethyl}amine, tris {2-(2-methoxyethoxymethoxy)ethyl}amine, tri s {2-(1-methoxyethoxy)ethyl}amine, tris {2-(1-ethoxyethoxy)ethyl}amine, tris{2-(1-ethoxypropoxy)ethyl}amine, tris[2-{2-(2-hydroxyethoxy)ethoxy}ethyl]amine and triethanolamine triacetate, and triethanolamine triacetate is preferable.

Examples of aromatic amines include 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole and derivatives thereof, as well as tribenzylamine, aniline compound and N-tert-butoxycarbonylpyrrolidine.

As the component (D1), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

Among the above examples, as the component (D1), an aromatic amine is preferable, and an aniline compound is more preferable. Examples of the aniline compound include 2,6-diisopropylaniline, N, N-dimethylaniline, N, N-dibutylaniline, and N, N-dihexylaniline.

When the resist composition contains the component (D1), the amount of the component (D1) is typically used in an amount within a range from 0.01 to 5 parts by weight, relative to 100 parts by weight of the component (A). When the amount of the component (D1) is within the above-mentioned preferable range, a good balance may be achieved with the other structural units, and the lithography properties may be improved.

Component (D2)

The component (D2) is not particularly limited, as long as it does not fall under the definition of the component (D0), and it is decomposed upon exposure and then loses the ability of controlling of acid diffusion. As the component (D2), at least one compound selected from the group consisting of a compound represented by general formula (d2-1) shown below (hereafter, referred to as “component (d2-1)”), a compound represented by general formula (d2-2) shown below (hereafter, referred to as “component (d2-2)”) and a compound represented by general formula (d1-3) shown below (hereafter, referred to as “component (d2-3)”) is preferably used.

At exposed portions of the resist film, the components (d2-1) to (d2-3) are decomposed and then lose the ability of controlling of acid diffusion (i.e., basicity), and therefore the components (d2-1) to (d2-3) cannot function as a quencher, whereas at unexposed portions, the components (d2-1) to (d2-3) functions as a quencher.

In the formulae, Rd¹ to Rd⁴ represent a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, provided that, the carbon atom adjacent to the sulfur atom within the Rd² in general formula (d2-2) has no fluorine atom bonded thereto; Yd¹ represents a single bond or a divalent linking group; m represents an integer of 1 or more, and each M′^(m+) independently represents an onium cation having a valency of m.

{Component (d2-1)}

Anion Moiety

In formula (d2-1), Rd¹ represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same groups as those defined above for R¹⁰¹ in the aforementioned formula (b-1).

Among these, as the group for Rd¹, an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent and a chain-like alkyl group which may have a substituent are preferable.

Examples of the substituent for these groups include a hydroxy group, an oxo group, an alkyl group, an aryl group, a fluorine atom, a fluorinated alkyl group, a lactone-containing cyclic group represented by any one of the aforementioned formulae (a2-r-1) to (a2-r-7), an ether bond, an ester bond, and a combination thereof. In the case where an ether bond or an ester bond is included as the substituent, the substituent may be bonded via an alkylene group, and a linking group represented by any one of the aforementioned formulae (y-al-1) to (y-al-5) is preferable as the substituent.

Preferable examples of the aromatic hydrocarbon group include a phenyl group, a naphthyl group, and a polycyclic structure (for example, a polycyclic structure formed of a ring structure having a bicyclooctane skeleton and a ring structure other than the bicyclooctane skeleton) containing a bicyclooctane skeleton.

Examples of the aliphatic cyclic group include groups in which one or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane.

The chain-like alkyl group preferably has 1 to 10 carbon atoms, and specific examples thereof include a linear alkyl group such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl or a decyl group, and a branched alkyl group such as a 1-methylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group or a 4-methylpentyl group.

In the case where the chain-like alkyl group is a fluorinated alkyl group having a fluorine atom or a fluorinated alkyl group, the fluorinated alkyl group preferably has 1 to 11 carbon atoms, more preferably 1 to 8 carbon atoms, and still more preferably 1 to 4 carbon atoms. The fluorinated alkyl group may contain an atom other than fluorine. Examples of the atom other than fluorine include an oxygen atom, a sulfur atom and a nitrogen atom.

As Rd¹, a fluorinated alkyl group in which part or all of the hydrogen atoms constituting a linear alkyl group have been substituted with fluorine atom(s) is preferable, and a fluorinated alkyl group in which all of the hydrogen atoms constituting a linear alkyl group have been substituted with fluorine atoms (i.e., a linear perfluoroalkyl group) is particularly desirable.

Specific examples of preferable anion moieties for the component (d2-1) are shown below.

Cation Moiety

In formula (d2-1), M′^(m+) represents an m-valent organic cation As the onium cation moiety for M′^(m+), cations represented by the aforementioned general formulae (ca-1) to (ca-4) may be mentioned as preferable examples. Specific examples include cations represented by the aforementioned chemical formulae (ca-1-1) to (ca-1-78) and (ca-1-101) to (ca-1-149).

As the component (d2-1), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

{Component (d2-2)}

Anion Moiety

In formula (d2-2), Rd² represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same groups as those defined above for R¹⁰¹ in the aforementioned formula (b-1).

However, the carbon atom adjacent to the sulfur atom within the Rd² has no fluorine atom bonded thereto. As a result, the anion of the component (d2-2) becomes an appropriately weak acid anion, thereby improving the quenching ability of the component (D2).

As Rd², a chain-like alkyl group which may have a substituent or an aliphatic cyclic group which may have a substituent is preferable. The chain-like alkyl group preferably has 1 to 10 carbon atoms, and more preferably 3 to 10 carbon atoms. As the aliphatic cyclic group, a group in which one or more hydrogen atoms have been removed from adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane or camphor (which may have a substituent) is more preferable.

The hydrocarbon group for Rd² may have a substituent. As the substituent, the same groups as those described above for substituting the hydrocarbon group (e.g., aromatic hydrocarbon group, aliphatic cyclic group, chain-like alkyl group) for Rd¹ in the formula (d2-1) can be mentioned.

Specific examples of preferable anion moieties for the component (d2-2) are shown below.

Cation Moiety

In formula (d2-2), M′^(m+) is an m-valent onium cation, and is the same as defined for M′^(m+) in the aforementioned formula (d2-1).

As the component (d2-2), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

{Component (d2-3)}

Anion Moiety

In formula (d2-3), Rd³ represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same groups as those defined above for R¹⁰¹ in the aforementioned formula (b-1), and a cyclic group containing a fluorine atom, a chain-like alkyl group or a chain-like alkenyl group is preferable. Among these, a fluorinated alkyl group is preferable, and more preferably the same fluorinated alkyl groups as those described above for Rd¹.

In formula (d2-3), Rd⁴ represents a cyclic group which may have a substituent, a chain-like alkyl group which may have a substituent or a chain-like alkenyl group which may have a substituent, and is the same groups as those defined above for R¹⁰¹ in the aforementioned formula (b-1).

Among these, an alkyl group which may have substituent, an alkoxy group which may have substituent, an alkenyl group which may have substituent or a cyclic group which may have substituent is preferable.

The alkyl group for Rd⁴ is preferably a linear or branched alkyl group of 1 to 5 carbon atoms, and specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group. Part of the hydrogen atoms within the alkyl group for Rd⁴ may be substituted with a hydroxy group, a cyano group or the like.

The alkoxy group for Rd⁴ is preferably an alkoxy group of 1 to 5 carbon atoms, and specific examples thereof include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group and a tert-butoxy group. Among these, a methoxy group and an ethoxy group are preferable.

As the alkenyl group for Rd⁴, the same groups as those described above for R¹⁰¹ in the aforementioned formula (b-1) may be mentioned, and a vinyl group, a propenyl group (an allyl group), a 1-methylpropenyl group and a 2-methylpropenyl group are preferable. These groups may have an alkyl group of 1 to 5 carbon atoms or a halogenated alkyl group of 1 to 5 carbon atoms as a substituent.

As the cyclic group for Rd⁴, the same groups as those described above for R¹⁰¹ in the aforementioned formula (b-1) may be mentioned. Among these, as the cyclic group, an alicyclic group (e.g., a group in which one or more hydrogen atoms have been removed from a cycloalkane such as cyclopentane, cyclohexane, adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane) or an aromatic group (e.g., a phenyl group or a naphthyl group) is preferable. When Rd⁴ is an alicyclic group, the resist composition can be satisfactorily dissolved in an organic solvent, thereby improving the lithography properties.

In formula (d2-3), Yd¹ represents a single bond or a divalent linking group. The divalent linking group for Yd¹ is not particularly limited, and examples thereof include a divalent hydrocarbon group (aliphatic hydrocarbon group, or aromatic hydrocarbon group) which may have a substituent and a divalent linking group containing a hetero atom. The divalent linking groups are the same as defined for the divalent hydrocarbon group which may have a substituent and the divalent linking group containing a hetero atom explained above as the divalent linking group for Ya^(x1) in the aforementioned formula (a10-1).

As Yd¹, a carbonyl group, an ester bond, an amide bond, an alkylene group or a combination of these is preferable. As the alkylene group, a linear or branched alkylene group is more preferable, and a methylene group or an ethylene group is still more preferable.

Specific examples of preferable anion moieties for the component (d2-3) are shown below.

Cation Moiety

In formula (d2-3), M′^(m+) is an m-valent onium cation, and is the same as defined for M′^(m+) in the aforementioned formula (d2-1).

As the component (d2-3), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

As the component (D2), one kind of the aforementioned components (d2-1) to (d2-3) may be used, or at least two kinds of the aforementioned components (d2-1) to (d2-3) may be used.

In the case where the resist composition contains the component (D2), the amount of the component (D2) relative to 100 parts by weight of the component (A) is preferably within a range from 0.5 to 35 parts by weight, more preferably from 1 to 25 parts by weight, still more preferably from 2 to 20 parts by weight, and still more preferably 3 to 15 parts by weight.

When the amount of the component (D2) is at least as large as the lower limit of the above-mentioned range, excellent lithography properties and excellent resist pattern shape can be more reliably obtained. On the other hand, when the amount of the component (D2) is no more than the upper limit of the above-mentioned preferable range, a good balance may be achieved with the other structural units, and the lithography properties may be improved.

Production Method of Component (D2):

The production methods of the components (d2-1) and (d2-2) are not particularly limited, and the components (d2-1) and (d2-2) may be produced by conventional methods.

Further, the production method of the component (d2-3) is not particularly limited, and the component (d2-3) may be produced in the same manner as disclosed in US2012-0149916.

In the resist composition of the present embodiment, as the component (D), the component (D2) is preferable, and the component (d2-1) is more preferable.

<<Component (E): At Least One Compound Selected from the Group Consisting of Organic Carboxylic Acids, and Phosphorus Oxo Acids and Derivatives Thereof>>

In the resist composition of the present embodiment, for preventing any deterioration in sensitivity, and improving the resist pattern shape and the post exposure stability of the latent image formed by the pattern-wise exposure of the resist layer, at least one compound (E) (hereafter referred to as the component (E)) selected from the group consisting of an organic carboxylic acid, or a phosphorus oxo acid or derivative thereof may be added.

Examples of suitable organic carboxylic acids include acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, and salicylic acid.

Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid and phosphinic acid. Among these, phosphonic acid is particularly desirable.

Examples of oxo acid derivatives include esters in which a hydrogen atom within the above-mentioned oxo acids is substituted with a hydrocarbon group. Examples of the hydrocarbon group include an alkyl group of 1 to 5 carbon atoms and an aryl group of 6 to 15 carbon atoms.

Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.

Examples of phosphonic acid derivatives include phosphonic acid esters such as dimethyl phosphonate, di-n-butyl phosphonate, phenylphosphonic acid, diphenyl phosphonate and dibenzyl phosphonate.

Examples of phosphinic acid derivatives include phosphinic acid esters and phenylphosphinic acid.

In the resist composition of the present embodiment, as the component (E), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

When the resist composition contains the component (E), the amount of the component (E) is typically used in an amount within a range from 0.01 to 5 parts by weight, relative to 100 parts by weight of the component (A).

<<Component (F): Fluorine Additive>>

In the present embodiment, the resist composition may further include a fluorine additive (hereafter, referred to as “component (F)”) for imparting water repellency to the resist film, or improving lithography properties.

As the component (F), for example, a fluorine-containing polymeric compound described in Japanese Unexamined Patent Application, First Publication No. 2010-002870, Japanese Unexamined Patent Application, First Publication No. 2010-032994, Japanese Unexamined Patent Application, First Publication No. 2010-277043, Japanese Unexamined Patent Application, First Publication No. 2011-13569, and Japanese Unexamined Patent Application, First Publication No. 2011-128226 can be used.

Specific examples of the component (F) include polymers having a structural unit (f1) represented by general formula (f1-1) shown below. As the polymer, a polymer (homopolymer) consisting of a structural unit (f1) represented by formula (f1-1) shown below; a copolymer of the structural unit (f1) and the aforementioned structural unit (a4); a copolymer of the structural unit (f1) and the aforementioned structural unit (a1); and a copolymer of the structural unit (f1), a structural unit derived from acrylic acid or methacrylic acid and the aforementioned structural unit (a1) are preferable. As the structural unit (a1) to be copolymerized with the structural unit (f1), a structural unit derived from 1-ethyl-1-cyclooctyl (meth)acrylate or a structural unit derived from 1-methyl-1-adamantyl (meth)acrylate is preferable.

In the formula, R is the same as defined above; Rf¹⁰² and Rf¹⁰³ each independently represents a hydrogen atom, a halogen atom, an alkyl group of 1 to 5 carbon atoms, or a halogenated alkyl group of 1 to 5 carbon atoms, provided that Rf¹⁰² and Rf¹⁰³ may be the same or different; nf¹ represents an integer of 0 to 5; and Rf¹⁰¹ represents an organic group containing a fluorine atom.

In formula (f1-1), R bonded to the carbon atom on the α-position is the same as defined above. As R, a hydrogen atom or a methyl group is preferable.

In formula (f1-1), examples of the halogen atom for Rf¹⁰² and Rf¹⁰³ include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable. Examples of the alkyl group of 1 to 5 carbon atoms for Rf¹⁰² and Rf¹⁰³ include the same alkyl group of 1 to 5 carbon atoms as those described above for R, and a methyl group or an ethyl group is preferable. Specific examples of the halogenated alkyl group of 1 to 5 carbon atoms represented by Rf¹⁰² or Rf¹⁰³ include groups in which part or all of the hydrogen atoms of the aforementioned alkyl groups of 1 to 5 carbon atoms have been substituted with halogen atoms.

Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly desirable. Among these examples, as Rf¹⁰² and Rf¹⁰³, a hydrogen atom, a fluorine atom or an alkyl group of 1 to 5 carbon atoms is preferable, and a hydrogen atom, a fluorine atom, a methyl group or an ethyl group is more preferable.

In formula (f1-1), nf¹ represents an integer of 0 to 5, preferably an integer of 0 to 3, and more preferably 0 or 1.

In formula (f1-1), Rf¹⁰¹ represents an organic group containing a fluorine atom, and is preferably a hydrocarbon group containing a fluorine atom.

The hydrocarbon group containing a fluorine atom may be linear, branched or cyclic, and preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms.

It is preferable that the hydrocarbon group having a fluorine atom has 25% or more of the hydrogen atoms within the hydrocarbon group fluorinated, more preferably 50% or more, and most preferably 60% or more, as the hydrophobicity of the resist film during immersion exposure is enhanced.

Among these, as Rf¹⁰¹, a fluorinated hydrocarbon group of 1 to 6 carbon atoms is preferable, and a trifluoromethyl group, —CH₂—CF₃, —CH₂—CF₂—CF₃, —CH(CF₃)₂, —CH₂—CH₂—CF₃, and —CH₂—CH₂—CF₂—CF₂—CF₂—CF₃ are most preferable.

The weight average molecular weight (Mw) (the polystyrene equivalent value determined by gel permeation chromatography) of the component (F) is preferably 1,000 to 50,000, more preferably 5,000 to 40,000, and most preferably 10,000 to 30,000. When the weight average molecular weight is no more than the upper limit of the above-mentioned range, the resist composition exhibits a satisfactory solubility in a resist solvent. On the other hand, when the weight average molecular weight is at least as large as the lower limit of the above-mentioned range, dry etching resistance and the cross-sectional shape of the resist pattern becomes satisfactory.

Further, the dispersity (Mw/Mn) of the component (F) is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.2 to 2.5.

In the resist composition of the present embodiment, as the component (F), one kind of compound may be used, or two or more kinds of compounds may be used in combination.

When the resist composition contains the component (F), the component (F) is used in an amount within a range from 0.5 to 10 parts by weight, relative to 100 parts by weight of the component (A).

<<Component (S): Organic Solvent>>

The resist composition of the present embodiment may be prepared by dissolving the resist materials for the resist composition in an organic solvent (hereafter, referred to as “component (S)”).

The component (S) may be any organic solvent which can dissolve the respective components to give a homogeneous solution, and any organic solvent can be appropriately selected from those which have been conventionally known as solvents for a chemically amplified resist composition.

Examples thereof include lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, 2-heptanone, ethylene carbonate and propylene carbonate; polyhydric alcohols, such as ethylene glycol, diethylene glycol, propylene glycol and dipropylene glycol; compounds having an ester bond, such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, and dipropylene glycol monoacetate; polyhydric alcohol derivatives including compounds having an ether bond, such as a monoalkylether (e.g., monomethylether, monoethylether, monopropylether or monobutylether) or monophenylether of any of these polyhydric alcohols or compounds having an ester bond (among these, propylene glycol monomethyl ether acetate (PGMEA) and propylene glycol monomethyl ether (PGME) are preferable); cyclic ethers such as dioxane; esters such as methyl lactate, ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, and ethyl ethoxypropionate; aromatic organic solvents such as anisole, ethylbenzylether, cresylmethylether, diphenylether, dibenzylether, phenetole, butylphenylether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene and mesitylene; and dimethylsulfoxide (DMSO).

In the resist composition of the present embodiment, as the component (S), one kind of solvent may be used, or two or more kinds of solvents may be used as a mixed solvent.

Among these, PGMEA, PGME, γ-butyrolactone, propylene carbonate, EL and cyclohexanone are preferable.

Further, among the mixed solvents, a mixed solvent obtained by mixing PGMEA with a polar solvent is preferable. The mixing ratio (weight ratio) of the mixed solvent can be appropriately determined, taking into consideration the compatibility of the PGMEA with the polar solvent, but is preferably in the range of 1:9 to 9:1, more preferably from 2:8 to 8:2.

Specifically, when EL or cyclohexanone is mixed as the polar solvent, the PGMEA:EL or cyclohexanone weight ratio is preferably from 1:9 to 9:1, and more preferably from 2:8 to 8:2. Alternatively, when PGME is mixed as the polar solvent, the PGMEA:PGME weight ratio is preferably from 1:9 to 9:1, more preferably from 2:8 to 8:2, and still more preferably 3:7 to 7:3. Furthermore, a mixed solvent of PGMEA, PGME and cyclohexanone is also preferable.

Alternatively, as the component (S), a mixed solvent of at least one member selected from PGMEA and EL and at least one member selected from γ-butyrolactone and propylene carbonate is preferable. The mixing ratio (former:latter) of such a mixed solvent is preferably from 60:40 to 99:1, and more preferably from 70:30 to 95:5.

The amount of the component (S) is not particularly limited, and is appropriately adjusted to a concentration which enables coating of a coating solution to a substrate. In general, the component (S) is used in an amount such that the solid content of the resist composition becomes within the range from 0.1 to 20% by weight, and preferably from 0.2 to 15% by weight.

If desired, other miscible additives may also be added to the resist composition of the present embodiment. Examples of such miscible additives include additive resins for improving the performance of the resist film, dissolution inhibitors, plasticizers, stabilizers, colorants, halation prevention agents, and dyes.

After dissolving the resist materials in the organic solvent (S), the resist composition of the present embodiment may have impurities or the like removed by using a polyimide porous film, a polyamide-imide porous film, or the like. For example, the resist composition may be subjected to filtration using a filter formed of a polyimide porous membrane, a filter formed of a polyamide-imide porous film, or a filter formed of a polyimide porous membrane and a polyamide-imide porous film. Examples of the polyimide porous membrane and the polyamide-imide porous film include those described in Japanese Unexamined Patent Application, First Publication No. 2016-155121.

The resist composition of the present embodiment includes the aforementioned components (A) and (D0), and any other optional components.

Preferable examples include a resist composition including the component (A), the component (D0), the component (B) and the component (S).

As described above, the resist composition of the present embodiment includes the resin component (A1) having the structural unit (a0), and the component (D0). The structural unit (a0) has an acid dissociable group represented by “—C^(t)(R¹¹)(R¹²)(R¹³)” in formula (a0-1). In the acid dissociable group “—C^(t)(R¹¹)(R¹²)(R¹³)”, the α-position of the tertiary carbon atom C^(t) is a carbon atom constituting a carbon-carbon unsaturated bond. Therefore, a carbocation which is formed when the acid dissociable group “—C^(t)(R¹¹)(R¹²)(R¹³)” is dissociated exhibits high stability, as compared to a carbocation which is formed when an acid dissociable group in which the α-position of the tertiary carbon atom C^(t) does not constitute a carbon atom constituting a carbon-carbon unsaturated bond is dissociated. As a result, the structural unit (a0) exhibits improved acid dissociability.

On the other hand, the component (D0) has an anion moiety with a specific structure, and the anion moiety contains at least one fluorine atom or fluorinated alkyl group as a substituent. Therefore, it is presumed that, when a resist film is formed using the resist composition of the present embodiment, the component (D0) is segregated on the surface of the resist film.

OoB light may enter the unexposed portion of the resist film as flare (stray light) (that is, the selectivity of the exposed area during EUV light irradiation is lost), and the acid generator component may be decomposed even in the unexposed portion. In such a case, the deprotection reaction of the protecting group may proceed at unexposed portions, and may cause deterioration of the contrast of the resist pattern, loss of film thickness, deterioration of roughness, pattern disconnection, and the like. In contrast, in a resist film formed using the resist composition of the present embodiment, it is presumed that the acid generated by flare is trapped by the component (D0) segregated at the surface of the resist film, so as to control diffusion of acid.

According to the resist composition of the present embodiment, by virtue of using a combination of the component (A1) and the component (D0), in the formation of a resist pattern, sensitivity may be enhanced, and a resist pattern exhibiting improved lithography properties and having a good shape may be formed.

(Method of Forming a Resist Pattern)

The method of forming a resist pattern according to the second aspect of the present invention includes: using a resist composition according to the first aspect to form a resist film on a substrate; exposing the resist film; and developing the exposed resist film to form a resist pattern.

The method for forming a resist pattern according to the present embodiment can be performed, for example, as follows.

Firstly, a resist composition of the first aspect is applied to a substrate using a spinner or the like, and a bake treatment (post applied bake (PAB)) is conducted at a temperature of 80 to 150° C. for 40 to 120 seconds, preferably 60 to 90 seconds, to form a resist film.

Following selective exposure of the thus formed resist film, either by exposure through a mask having a predetermined pattern formed thereon (mask pattern) using an exposure apparatus such an electron beam lithography apparatus or an EUV exposure apparatus, or by patterning via direct irradiation with an electron beam without using a mask pattern, baking treatment (post exposure baking (PEB)) is conducted under temperature conditions of 80 to 150° C. for 40 to 120 seconds, and preferably 60 to 90 seconds.

Next, the resist film is subjected to a developing treatment. The developing treatment is conducted using an alkali developing solution in the case of an alkali developing process, and a developing solution containing an organic solvent (organic developing solution) in the case of a solvent developing process.

After the developing treatment, it is preferable to conduct a rinse treatment. The rinse treatment is preferably conducted using pure water in the case of an alkali developing process, and a rinse solution containing an organic solvent in the case of a solvent developing process.

In the case of a solvent developing process, after the developing treatment or the rinsing, the developing solution or the rinse liquid remaining on the pattern can be removed by a treatment using a supercritical fluid.

After the developing treatment or the rinse treatment, drying is conducted. If desired, bake treatment (post bake) can be conducted following the developing.

In this manner, a resist pattern can be formed.

The substrate is not specifically limited and a conventionally known substrate can be used. For example, substrates for electronic components, and such substrates having wiring patterns formed thereon can be used. Specific examples of the material of the substrate include metals such as silicon wafer, copper, chromium, iron and aluminum; and glass. Suitable materials for the wiring pattern include copper, aluminum, nickel, and gold.

Further, as the substrate, any one of the above-mentioned substrates provided with an inorganic and/or organic film on the surface thereof may be used. As the inorganic film, an inorganic antireflection film (inorganic BARC) can be used. As the organic film, an organic antireflection film (organic BARC) and an organic film such as a lower-layer organic film used in a multilayer resist method can be used.

Here, a “multilayer resist method” is method in which at least one layer of an organic film (lower-layer organic film) and at least one layer of a resist film (upper resist film) are provided on a substrate, and a resist pattern formed on the upper resist film is used as a mask to conduct patterning of the lower-layer organic film. This method is considered as being capable of forming a pattern with a high aspect ratio. More specifically, in the multilayer resist method, a desired thickness can be ensured by the lower-layer organic film, and as a result, the thickness of the resist film can be reduced, and an extremely fine pattern with a high aspect ratio can be formed.

The multilayer resist method is broadly classified into a method in which a double-layer structure consisting of an upper-layer resist film and a lower-layer organic film is formed (double-layer resist method), and a method in which a multilayer structure having at least three layers consisting of an upper-layer resist film, a lower-layer organic film and at least one intermediate layer (thin metal film or the like) provided between the upper-layer resist film and the lower-layer organic film (triple-layer resist method).

The wavelength to be used for exposure is not particularly limited and the exposure can be conducted using radiation such as ArF excimer laser, KrF excimer laser, F₂ excimer laser, extreme ultraviolet rays (EUV), vacuum ultraviolet rays (VUV), electron beam (EB), X-rays, and soft X-rays. The resist composition of the present embodiment is effective to KrF excimer laser, ArF excimer laser, EB and EUV, and more effective to ArF excimer laser, EB and EUV, and most effective to EB and EUV. That is, the method of forming a resist pattern according to the present embodiment is effective in the case where the step of exposing the resist film includes exposing the resist film with extreme ultraviolet rays (EUV) or electron beam (EB).

The exposure of the resist film can be either a general exposure (dry exposure) conducted in air or an inert gas such as nitrogen, or immersion exposure (immersion lithography).

In immersion lithography, the region between the resist film and the lens at the lowermost point of the exposure apparatus is pre-filled with a solvent (immersion medium) that has a larger refractive index than the refractive index of air, and the exposure (immersion exposure) is conducted in this state.

The immersion medium preferably exhibits a refractive index larger than the refractive index of air but smaller than the refractive index of the resist film to be exposed. The refractive index of the immersion medium is not particularly limited as long as it satisfies the above-mentioned requirements.

Examples of this immersion medium which exhibits a refractive index that is larger than the refractive index of air but smaller than the refractive index of the resist film include water, fluorine-based inert liquids, silicon-based solvents and hydrocarbon-based solvents.

Specific examples of the fluorine-based inert liquids include liquids containing a fluorine-based compound such as C₃HCl₂F₅, C₄F₉OCH₃, C₄F₉OC₂H₅ or C₅H₃F₇ as the main component, which have a boiling point within a range from 70 to 180° C. and preferably from 80 to 160° C. A fluorine-based inert liquid having a boiling point within the above-mentioned range is advantageous in that the removal of the immersion medium after the exposure can be conducted by a simple method.

As a fluorine-based inert liquid, a perfluoroalkyl compound in which all of the hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly desirable. Examples of these perfluoroalkyl compounds include perfluoroalkylether compounds and perfluoroalkylamine compounds.

Specifically, one example of a suitable perfluoroalkylether compound is perfluoro(2-butyl-tetrahydrofuran) (boiling point 102° C.), and an example of a suitable perfluoroalkylamine compound is perfluorotributylamine (boiling point 174° C.).

As the immersion medium, water is preferable in terms of cost, safety, environment and versatility.

As an example of the alkali developing solution used in an alkali developing process, a 0.1 to 10% by weight aqueous solution of tetramethylammonium hydroxide (TMAH) can be given.

As the organic solvent contained in the organic developing solution used in a solvent developing process, any of the conventional organic solvents can be used which are capable of dissolving the component (A) (prior to exposure). Specific examples of the organic solvent include polar solvents such as ketone solvents, ester solvents, alcohol solvents, nitrile solvents, amide solvents and ether solvents, and hydrocarbon solvents.

A ketone solvent is an organic solvent containing C—C(═O)—C within the structure thereof. An ester solvent is an organic solvent containing C—C(═O)—O—C within the structure thereof. An alcohol solvent is an organic solvent containing an alcoholic hydroxy group in the structure thereof. An “alcoholic hydroxy group” refers to a hydroxy group bonded to a carbon atom of an aliphatic hydrocarbon group. A nitrile solvent is an organic solvent containing a nitrile group in the structure thereof. An amide solvent is an organic solvent containing an amide group within the structure thereof. An ether solvent is an organic solvent containing C—O—C within the structure thereof.

Some organic solvents have a plurality of the functional groups which characterizes the aforementioned solvents within the structure thereof. In such a case, the organic solvent can be classified as any type of the solvent having the characteristic functional group. For example, diethyleneglycol monomethylether can be classified as either an alcohol solvent or an ether solvent.

A hydrocarbon solvent consists of a hydrocarbon which may be halogenated, and does not have any substituent other than a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.

As the organic solvent contained in the organic developing solution, among these, a polar solvent is preferable, and ketone solvents, ester solvents and nitrile solvents are preferable.

Examples of ketone solvents include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, acetone, 4-heptanone, 1-hexanone, 2-hexanone, diisobutyl ketone, cyclohexanone, methylcyclohexanone, phenylacetone, methyl ethyl ketone, methyl isobutyl ketone, acetylacetone, acetonylacetone, ionone, diacetonylalcohol, acetylcarbinol, acetophenone, methyl naphthyl ketone, isophorone, propylenecarbonate, γ-butyrolactone and methyl amyl ketone (2-heptanone). Among these examples, as a ketone solvent, methyl amyl ketone (2-heptanone) is preferable.

Examples of ester solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, amyl acetate, isoamyl acetate, ethyl methoxyacetate, ethyl ethoxyacetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol monopropyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monophenyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monopropyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monophenyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, 2-methoxybutyl acetate, 3-methoxybutyl acetate, 4-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, 3-ethyl-3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, 2-ethoxybutyl acetate, 4-ethoxybutyl acetate, 4-propoxybutyl acetate, 2-methoxypentyl acetate, 3-methoxypentyl acetate, 4-methoxypentyl acetate, 2-methyl-3-methoxypentyl acetate, 3-methyl-3-methoxypentyl acetate, 3-methyl-4-methoxypentyl acetate, 4-methyl-4-methoxypentyl acetate, propylene glycol diacetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, propyl lactate, ethyl carbonate, propyl carbonate, butyl carbonate, methyl pyruvate, ethyl pyruvate, propyl pyruvate, butyl pyruvate, methyl acetoacetate, ethyl acetoacetate, methyl propionate, ethyl propionate, propyl propionate, isopropyl propionate, methyl 2-hydroxypropionate, ethyl 2-hydroxypropionate, methyl-3-methoxypropionate, ethyl-3-methoxypropionate, ethyl-3-ethoxypropionate and propyl-3-methoxypropionate. Among these examples, as an ester solvent, butyl acetate is preferable.

Examples of nitrile solvents include acetonitrile, propionitrile, valeronitrile, butyronitrile and the like.

If desired, the organic developing solution may have a conventional additive blended. Examples of the additive include surfactants. The surfactant is not particularly limited, and for example, an ionic or non-ionic fluorine and/or silicon surfactant can be used.

As the surfactant, a non-ionic surfactant is preferable, and a non-ionic fluorine surfactant or a non-ionic silicon surfactant is more preferable.

When a surfactant is added, the amount thereof based on the total amount of the organic developing solution is generally 0.001 to 5% by weight, preferably 0.005 to 2% by weight, and more preferably 0.01 to 0.5% by weight.

The developing treatment can be performed by a conventional developing method. Examples thereof include a method in which the substrate is immersed in the developing solution for a predetermined time (a dip method), a method in which the developing solution is cast up on the surface of the substrate by surface tension and maintained for a predetermined period (a puddle method), a method in which the developing solution is sprayed onto the surface of the substrate (spray method), and a method in which the developing solution is continuously ejected from a developing solution ejecting nozzle while scanning at a constant rate to apply the developing solution to the substrate while rotating the substrate at a constant rate (dynamic dispense method).

As the organic solvent contained in the rinse liquid used in the rinse treatment after the developing treatment in the case of a solvent developing process, any of the aforementioned organic solvents contained in the organic developing solution can be used which hardly dissolves the resist pattern. In general, at least one solvent selected from the group consisting of hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. Among these, at least one solvent selected from the group consisting of hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents and amide solvents is preferable, more preferably at least one solvent selected from the group consisting of alcohol solvents and ester solvents, and an alcohol solvent is particularly desirable.

The alcohol solvent used for the rinse liquid is preferably a monohydric alcohol of 6 to 8 carbon atoms, and the monohydric alcohol may be linear, branched or cyclic. Specific examples thereof include 1-hexanol, 1-heptanol, 1-octanol, 2-hexanol, 2-heptanol, 2-octanol, 3-hexanol, 3-heptanol, 3-octanol, 4-octanol and benzyl alcohol. Among these, 1-hexanol, 2-heptanol and 2-hexanol are preferable, and 1 hexanol and 2-hexanol are more preferable.

As the organic solvent, one kind of solvent may be used alone, or two or more kinds of solvents may be used in combination. Further, an organic solvent other than the aforementioned examples or water may be mixed together. However, in consideration of the development characteristics, the amount of water within the rinse liquid, based on the total amount of the rinse liquid is preferably 30% by weight or less, more preferably 10% by weight or less, still more preferably 5% by weight or less, and most preferably 3% by weight or less.

If desired, the rinse solution may have a conventional additive blended. Examples of the additive include surfactants. Examples of the additive include surfactants. As the surfactant, the same surfactants as those described above can be mentioned, a non-ionic surfactant is preferable, and a non-ionic fluorine surfactant or a non-ionic silicon surfactant is more preferable.

When a surfactant is added, the amount thereof based on the total amount of the rinse liquid is generally 0.001 to 5% by weight, preferably 0.005 to 2% by weight, and more preferably 0.01 to 0.5% by weight.

The rinse treatment using a rinse liquid (washing treatment) can be conducted by a conventional rinse method. Examples of the rinse method include a method in which the rinse liquid is continuously applied to the substrate while rotating it at a constant rate (rotational coating method), a method in which the substrate is immersed in the rinse liquid for a predetermined time (dip method), and a method in which the rinse liquid is sprayed onto the surface of the substrate (spray method).

In the method of forming a resist pattern according to the present embodiment, by virtue of using the resist composition of the first aspect, it becomes possible to enhance sensitivity in the formation of a resist pattern, and a resist pattern having improved lithography properties and a good pattern shape can be formed.

Examples

As follows is a description of examples of the present invention, although the scope of the present invention is by no way limited by these examples.

In the following examples, a compound represented by a chemical formula (1) is denoted as “compound (1)”, and the same applies for compounds represented by other chemical formulae.

Production Examples of Copolymers (A1-1) to (A1-6), Copolymers (A2-1) to (A2-3)

Each of copolymers (A1-1) to (A1-6) and (A2-1) to (A2-3) were obtained by a conventional radical polymerization using monomers for deriving structural units which constitute each copolymer with a predetermined molar ratio.

The obtained copolymers (A1-1) to (A1-6), copolymers (A2-1) to (A2-3) are shown below.

With respect to each copolymer, the compositional ratio of the polymers (the molar ratio of the respective structural units in the polymeric compound) as determined by ¹³C-NMR, the weight average molecular weight (Mw) and the polydispersity (Mw/Mn) determined by the polystyrene equivalent value as measured by GPC are also shown in Table 1.

TABLE 1 Weight average Compositional ratio of molecular weight Polydispersity Copolymer copolymer (molar ratio) (Mw) (Mw/Mn) (A1-1) l/m = 50/50 6700 1.71 (A1-2) l/m = 50/50 7200 1.71 (A1-3) l/m = 50/50 6800 1.67 (A1-4) l/m = 50/50 6700 1.71 (A1-5) l/m/n = 50/15/35 7000 1.71 (A1-6) l/m/n = 40/10/50 6900 1.71 (A2-1) l/m = 50/50 7000 1.70 (A2-2) l/m/n = 50/15/35 6900 1.72 (A2-3) l/m/n = 40/10/50 7200 1.71

<Production of Resist Composition>

Examples 1 to 7, Comparative Examples 1 to 5

The components shown in Table 2 were mixed together and dissolved to obtain each resist composition.

TABLE 2 Com- Com- Component (D) ponent ponent Component Component Component (A) (B) (D0) (D2) (S) Example 1 (A1)-1 (B1)-1 (D0)-1 — (S)-1 [100] [14.0] [4.5] [6400] Example 2 (A1)-2 (B1)-1 (D0)-2 — (S)-1 [100] [14.0] [4.4] [6400] Example 3 (A1)-3 (B1)-1 (D0)-3 — (S)-1 [100] [14.0] [3.9] [6400] Example 4 (A1)-4 (B1)-1 (D0)-2 — (S)-1 [100] [14.0] [4.4] [6400] Example 5 (A1)-1 (B1)-1 (D0)-4 — (S)-1 [100] [14.0] [4.3] [6400] Comparative (A1)-1 (B1)-1 — (D2)-1 (S)-1 Example 1 [100] [14.0] [3.8] [6400] Comparative (A2)-1 (B1)-1 (D0)-2 — (S)-1 Example 2 [100] [14.0] [4.4] [6400] Comparative (A1)-1 (B1)-1 — (D2)-2 (S)-1 Example 3 [100] [14.0] [3.7] [6400] Example 6 (A1)-5 (B1)-1 (D0)-2 — (S)-1 [100] [14.0] [4.4] [6400] Example 7 (A1)-6 (B1)-1 (D0)-5 — (S)-1 [100] [14.0] [3.9] [6400] Comparative (A2)-2 (B1)-1 (D0)-2 — (S)-1 Example 4 [100] [14.0] [4.4] [6400] Comparative (A2)-3 (B1)-1 (D0)-5 — (S)-1 Example 5 [100] [14.0] [3.9] [6400]

In Table 2, the reference characters indicate the following. The values in brackets [ ] indicate the amount (in terms of parts by weight) of the component added.

(A1)-1 to (A1)-6: The above copolymers (A1-1) to (A1-6)

(A2)-1 to (A2)-3: The above copolymers (A2-1) to (A2-3)

(B1)-1: an acid generator represented by chemical formula (B1)-1 shown below

(D0)-1 to (D0)-5: Acid diffusion control agents consisting of compounds represented by chemical formulae (D0-1) to (D0-5) shown below, respectively.

(D2)-1 to (D2)-2: Acid diffusion control agents consisting of compounds represented by chemical formulae (D2-1) to (D2-2) shown below, respectively.

(S)-1: a mixed solvent of propylene glycol monomethyl ether acetate/propylene glycol monomethyl ether=60/40 (weight ratio).

<Formation of Resist Pattern>

Each of the resist compositions of examples and comparative examples was applied to an 8-inch silicon substrate which had been treated with hexamethyldisilazane (HMDS) using a spinner, and was then prebaked (PAB) on a hot plate at 110° C. for 60 seconds and dried, thereby forming a resist film having a film thickness of 30 nm.

A drawing (exposure) was carried out on the resist film using an electron beam lithography system JEOL-JBX-9300FS (manufactured by JEOL Ltd.) with acceleration voltage of 100 kV and a target size of a line-and-space pattern (hereinafter referred to as an “LS pattern”) having a line width of 50 nm and a pitch of 100 nm. Then, a post exposure bake (PEB) treatment was conducted at 90° C. for 60 seconds.

Thereafter, alkali developing was conducted for 60 seconds at 23° C. in a 2.38% by weight aqueous solution of tetramethylammonium hydroxide (TMAH) (product name: NMD-3; manufactured by Tokyo Ohka Kogyo Co., Ltd.).

As a result, an LS pattern having a line width of 50 nm and a pitch of 100 nm was formed.

[Evaluation of Optimum Exposure Dose (Eop)]

The optimum exposure dose Eop (C/cm²) with which the LS pattern was formed in the above formation of resist pattern was determined. The results are indicated under “Eop (ρC/cm²)” in Table 3.

[Evaluation of Line Width Roughness (LWR)]

With respect to the LS pattern formed in the above “formation of resist pattern”, 3σ was determined as a yardstick for indicating LWR. The results are indicated under “LWR (nm)” in Table 3.

“3σ” indicates a value of 3 times the standard deviation (σ) (i.e., 3σ) (unit: nm) determined by measuring the line positions at 400 points in the lengthwise direction of the line using a scanning electron microscope (product name: S-9380, manufactured by Hitachi High-Technologies Corporation; acceleration voltage: 800V).

The smaller this 30 value is, the lower the level of roughness on the side walls of the line, indicating that an LS pattern with a uniform width was obtained.

[Evaluation of Pattern Disconnection]

From the optimum exposure dose Eop with which an LS pattern having the target size could be formed, the exposure dose was gradually increased to form an LS pattern, and the minimum size of the pattern which could be resolved without pattern disconnection (defects in the line width direction of the LS pattern as viewed from the upper side of the LS pattern) was determined using a scanning electron microscope (product name: S-9380, manufactured by Hitachi High-Technologies Corporation) The results are indicated under “pattern disconnection suppressed minimum CD (nm)” in Table 3.

TABLE 3 Pattern disconnection suppressed Eop LWR minimum CD [μC/cm²] (nm) [nm] Example 1 90 5.2 35 Example 2 80 5.4 37 Example 3 90 5.3 35 Example 4 85 5.3 34 Example 5 95 5.5 38 Comparative 105 6.2 42 Example 1 Comparative 110 6.8 43 Example 2 Comparative 115 6.7 43 Example 3 Example 6 95 5.4 36 Example 7 90 5.2 35 Comparative 110 6.3 44 Example 4 Comparative 110 6.2 41 Example 5

From the results shown in Table 3, it was confirmed that, according to the resist composition of examples which applied the present invention, in the formation of a resist pattern, sensitivity could be improved, and a resist pattern could be formed with reduced roughness and suppressed pattern disconnection.

While preferred embodiments of the invention have been described and illustrated above, it should be understood that these are exemplary of the invention and are not to be considered as limiting. Additions, omissions, substitutions, and other modifications can be made without departing from the spirit or scope of the present invention. Accordingly, the invention is not to be considered as being limited by the foregoing description, and is only limited by the scope of the appended claims. 

What is claimed is:
 1. A resist composition which generates acid upon exposure and exhibits changed solubility in a developing solution under action of acid, the resist composition comprising: a resin component (A1) which exhibits changed solubility in a developing solution under action of acid, and a compound (D0) represented by general formula (d0) shown below, the resin component (A1) comprising a structural unit (a0) in which a compound represented by general formula (a0-1) has a polymerizable group within the W¹ portion converted into a main chain:

wherein, in formula (d0), Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group; Rd⁰² represents a substituent; q represents an integer of 0 to 3; n1 represents an integer of 1 or more; n2 represents an integer of 0 or more; provided that n1+n2≤(q×2)+5; m represents an integer of 1 or more, and M^(m+) represents an m-valent organic cation; in formula (a0-1), W¹ represents a polymerizable group-containing group; C^(t) represents a tertiary carbon atom, and the α-position of C^(t) is a carbon atom which constitutes a carbon-carbon unsaturated bond; R¹¹ represents an aromatic hydrocarbon group which may have a substituent, or a chain hydrocarbon group; R¹² and R¹³ each independently represents a chain hydrocarbon group which may have a substituent, or R¹² and R¹³ are mutually bonded to form a cyclic group which may have a substituent.
 2. The resist composition according to claim 1, wherein the compound (D0) comprises a compound represented by general formula (d0-1) shown below:

wherein R^(d11) represents an aryl group which may have a substituent; R^(d12) and R^(d13) each independently represents an aryl group which may have a substituent, or R^(d12) and R^(d13) are mutually bonded to form a ring with the sulfur atom; Rd⁰¹ represents a fluorine atom or a fluorinated alkyl group; Rd⁰² represents a substituent; q represents an integer of 0 to 3; n1 represents an integer of 1 or more; n2 represents an integer of 0 or more; provided that n1+n2≤(q×2)+5; m represents an integer of 1 or more.
 3. The resist composition according to claim 1, wherein —C^(t)(R¹¹)(R¹²)(R¹³) in general formula (a0-1) is a group represented by general formula (a0-r-1) shown below, a group represented by general formula (a0-r-2) shown below, and a group represented by general formula (a0-r-3) shown below:

wherein, in formula (a0-r-1), Ra′¹¹⁰ represents a linear or branched alkyl group having 1 to 12 carbon atoms optionally having part thereof substituted with a halogen atom or a hetero atom-containing group; Ra′¹¹¹ represents a group which forms an aliphatic cyclic group together with the carbon atom to which Ra′¹¹⁰ is bonded, or a group which forms a condensed polycyclic hydrocarbon group containing an aliphatic ring, together with the carbon atom to which Ra′¹¹⁰ is bonded; wherein part or all of the hydrogen atoms of the aliphatic cyclic group or the condensed polycyclic hydrocarbon group may be substituted; provided that, in the aliphatic cyclic group or the condensed polycyclic hydrocarbon group, the α-position of the carbon atom bonded to Ra′¹¹⁰ is a carbon atom constituting a carbon-carbon unsaturated bond; in formula (a0-r-2), C^(t) represents a tertiary carbon atoms; Xa represents an aliphatic cyclic group together with C^(t); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰¹ to Ra⁰³ each independently represents a hydrogen atom, a monovalent saturated chain hydrocarbon group of 1 to 10 carbon atoms or a monovalent saturated aliphatic cyclic hydrocarbon group of 3 to 20 carbon atoms; wherein part or all of the hydrogen atoms of the saturated chain hydrocarbon or the saturated aliphatic cyclic hydrocarbon may be substituted; 2 or more of Ra⁰¹ to Ra³ may be mutually bonded to form an aliphatic cyclic structure, but does not form a bridged structure; in formula (a0-r-3), C^(t) represents a tertiary carbon atoms; Xaa represents an aliphatic cyclic group together with ^(CT); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰⁴ represents an aromatic hydrocarbon group which may have a substituent; and * represents a bonding site.
 4. The resist composition according to claim 2, wherein —C^(t)(R¹¹)(R¹²)(R¹³) in general formula (a0-1) is a group represented by general formula (a0-r-1) shown below, a group represented by general formula (a0-r-2) shown below, and a group represented by general formula (a0-r-3) shown below:

wherein, in formula (a0-r-1), Ra′¹¹⁰ represents a linear or branched alkyl group having 1 to 12 carbon atoms optionally having part thereof substituted with a halogen atom or a hetero atom-containing group; Ra′¹¹¹ represents a group which forms an aliphatic cyclic group together with the carbon atom to which Ra′¹¹⁰ is bonded, or a group which forms a condensed polycyclic hydrocarbon group containing an aliphatic ring, together with the carbon atom to which Ra′¹¹⁰ is bonded; wherein part or all of the hydrogen atoms of the aliphatic cyclic group or the condensed polycyclic hydrocarbon group may be substituted; provided that, in the aliphatic cyclic group or the condensed polycyclic hydrocarbon group, the α-position of the carbon atom bonded to Ra′¹¹⁰ is a carbon atom constituting a carbon-carbon unsaturated bond; in formula (a0-r-2), C^(t) represents a tertiary carbon atoms; Xa represents an aliphatic cyclic group together with C^(t); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰¹ to Ra⁰³ each independently represents a hydrogen atom, a monovalent saturated chain hydrocarbon group of 1 to 10 carbon atoms or a monovalent saturated aliphatic cyclic hydrocarbon group of 3 to 20 carbon atoms; wherein part or all of the hydrogen atoms of the saturated chain hydrocarbon or the saturated aliphatic cyclic hydrocarbon may be substituted; 2 or more of Ra⁰¹ to Ra⁰³ may be mutually bonded to form an aliphatic cyclic structure, but does not form a bridged structure; in formula (a0-r-3), C^(t) represents a tertiary carbon atoms; Xaa represents an aliphatic cyclic group together with ^(CT); wherein part or all of the hydrogen atoms of the aliphatic cyclic group may be substituted; Ra⁰⁴ represents an aromatic hydrocarbon group which may have a substituent; and * represents a bonding site.
 5. A method of forming a resist pattern, including: using a resist composition of to form a resist film, exposing the resist film, and developing the exposed resist film to form a resist pattern.
 6. The resist pattern forming method according to claim 5, wherein the resist film is exposed to extreme ultraviolet (EUV) or electron beam (EB) in exposing the resist film. 